Improving adsorption performance of l

Scientific Reports volume 13, Article number: 10860 (2023) Cite this article

380 Accesses

Metrics details

In this research, rice husk (RH) was utilized to prepare a magnetic adsorbent for adsorption of ascorbic acid (AA). The magnetic agent is iron(III) chloride (FeCl3). The impact of acid concentration in the range of 400–800 ppm, adsorbent dosage in the range of 0.5–1 g, and contact time in the range of 10–130 min were studied. The Langmuir model had the highest R2 of 0.9982, 0.9996, and 0.9985 at the temperature of 15, 25, and 35 °C, respectively, and the qmax values in these temperatures have been calculated at 19.157, 31.34, and 38.75 mg/g, respectively. The pseudo-second-order kinetic model had the best agreement with the experimental results. In this kinetic model, the values of q have been measured at 36.496, 45.248, and 49.019 mg/g at the acid concentration of 418, 600, and 718 ppm, respectively. The values of ΔHo and ΔSo were measured 31.972 kJ/mol and 120.253 kJ/mol K, respectively, which proves the endothermic and irregularity nature of the adsorption of AA. Besides, the optimum conditions of the design-expert software have been obtained 486.929 ppm of acid concentration, 0.875 g of the adsorbent dosage, and 105.397 min of the contact time, and the adsorption efficiency in these conditions was determined at 92.94%. The surface area of the RH and modified RH was determined of 98.17 and 120.23 m2/g, respectively, which confirms the high surface area of these two adsorbents.

Vitamins have been broadly employed in the pharmaceutical, cosmetic, and food industries1. Types of vitamins are divided into two classes in view of their solubility in fat and water. The soluble vitamins in the water are thiamine (B1), riboflavin (B2), niacin (B3), pyridoxine (B6), pantothenic acid (B5), biotin (B7), folic acid (B9), cyanocobalamin (B12) and vitamin C. Vitamin C or l-Ascorbic acid (AA) is one of the imperative vitamins that posse remarkable antioxidant properties which can prevent radical reactions in the body whose damage cells and tissues. Thus, this vitamin can boost the immunity system2. Its deficiency can cause a risk of incurable illnesses such as cancer, heart disease, and cataracts3,4,5. Vitamin C is able to prevent microbial activity in food because of having a low-value pH6. Nevertheless, the body mechanism of people cannot able to produce vitamin C owing to the absence of l-gluconolactone enzyme and cannot retain this vital agent in the organism. Therefore, adequate content of this vitamin must enter the body through eating some food such as citrus fruits, berries, potatoes, tomatoes, peppers, broccoli, and spinach7. Bioactive compounds such as biomolecules used in various industries are often synthetic and are produced during diverse stages of the biotechnology and chemical process. Therefore, separation and purification of this vitamin from an aqueous solution is inevitable.

Diverse separation procedures exist. Each of these procedures has a number of drawbacks and can exert issues during the separation process. For instance, the precipitation procedure cannot able to treat the low concentration of metallic ions, and this method also can widely produce useless materials; microbial electrochemical technology (MET) has a remarkable elimination yield, nevertheless, this method requires a long period of time for eliminating the metallic ions; moreover, the price of the resins in the ion-exchange procedure is exorbitant8. Among the separation techniques, adsorption is one of the well-known methods due to the simplicity of performance, tremendous yield, easy recovery, and suitable price. Hence, the batch adsorption method was chosen for this study. Several types of reagents have been exploited as the adsorbent for the removal of metallic ions from contaminated water such as activated carbon9, fruit wastes10, mineral substances11,12,13,14, microbes15, waste materials16, and polymers17. In this study, a kind of agricultural waste was used as a natural adsorbent. The annual production of food and crop waste is increasing extensively, thus, it is crucial to manage food waste18. For avoiding this challenge, food waste can be converted into beneficial materials. The reuse of agricultural waste is proposed as a convenient and economical approach. Due to the desired performances and the low price of agricultural waste such as banana peel, orange peel, rice husk (RH), tea pulp, walnut shell19, Montmorillonite clay20, chicken beak21, zeolite22, and etc., these materials have received much attention. Also, various reagents can be grafted to the structure of the adsorbents for improving their performance such as polymers, metal hydroxide, acids, iron, and other chemical materials like xanthate23,24. Some valuable works that demonstrate the superiority of the modified adsorbent over the raw ones are indicated as follows. Foroutan et al. used walnut shell (WSA) and WSA/Starch/Fe3O4 for the removal of copper ions from the water. The uptake capacity of the copper ions was attained at 29 and 45.4 mg/g for WSA and WSA/Starch/Fe3O4, respectively19. Ahmadi et al. used Montmorillonite clay (MC) and MC/starch/CoFe2O4 for the removal of methylene blue (MB) and methyl violet (MV) from the wastewater. The uptake capacity of MV using MC and MC/starch/CoFe2O4 nanocomposite were 29.76 and 43.95 mg/g, respectively, and the uptake sorption capacity of MB using these sorbents were 31.96 and 47.51 mg/g, respectively20. Foroutan et al. studied the performance of a chicken beak containing hydroxyapatite (HApB) and modified one with the zeolitic imidazolate framework-8 (ZIF-8) for the removal of nickel ions from the water. The uptake capacity of nickel ions has been obtained at 24.27 and 63.49 mg/g using HApB and HApB/ ZIF-8, respectively21. Savari et al. investigated the removal of fluoride from the water using zeolite-zirconium under pulsed and continuous sonication. The uptake capacity of the fluoride has been calculated at 32.98 and 31.73 mg/g at the pulsed and continuous situations, respectively22. It was concluded that the modification with the magnetic particles has the most impact on the uptake capacity relative to the other modifiers. The magnetic materials especially magnetic biochars are in the category of carbon which can remove the pollutants by electrostatic attraction between the pollutants and oxygen-containing functional groups. Additionally, the generation of magnetic biochar at a minimal oxygen supply increases the crystalline architecture of this adsorbent owing to its graphitic domains that are much smaller in comparison with the nanocarbon materials. Magnetic materials have some benefits including: (1) They can be synthesized in one step only causes decreasing energy loss, (2) They have a flexible and exclusive property due to their surface area, high adsorption capacity, and high degree of surface reactivity, (3) They are mostly known as the economic and cost-effective adsorbents, and (4) They can reduce the concentration of the toxic gases, metallic ions, and other pollutants dramatically25.

The RH and modified RH were exploited as the adsorbents mostly for the removal of different dyes, and heavy metal ions. In addition, it was observed that the RH could be employed for the adsorption of some drugs such as paracetamol and tetracycline (Table 1). The use of RH and modified RH for the adsorption of AA has not been observed until now. Homagai et al. used modified RH for the removal of the crystal violet (CV) dye. The modification agent was xanthate. The highest adsorption capacity has been determined at 90.02 mg/g at a pH of 10 and a contact time of 60 min26. Bansal et al. used raw RH for the elimination of Cd(II) ions. The adsorption capacity was obtained at 3.83 mg/g at a pH of 2, and a time of 180 min27. Chowdhury et al. adsorbed malachite green using NaOH-rice husk. In their work, the uptake capacity has been obtained at 10 mg/g28. El-Shafey used sulfuric acid-rice husk for the removal of Se(IV) ions with an uptake capacity of 12 mg/g29. Hsu et al. removed the methacrylic acid using carboxyl-rice husk with an uptake capacity of 317.70 mg/g after 45 min30. Chen et al. could adsorb tetracycline after 40 min with an uptake capacity of 8.37 mg/g31. The other studies were brought in Table 1.

The objective of the present work was to exploit magnetic RH for trapping vitamin C from an aqueous solution. One of the strengths of this manuscript is the adsorption of vitamin C from an aqueous solution for the first time. The novelty of this work is using agricultural waste as a cost-effective and environmentally friendly adsorbent for reducing the AA from the pharmaceutical and food industries. It will help the industries for adsorbing the AA from the effluents and afterward leaching the AA from this adsorbent and using AA again in the production cycle. The other novelty is detecting the optimum point of the effective factors for increasing the yield using design-expert software. For this aim, various effective parameters including AA concentration, the dosage of the adsorbent, and contact time have been evaluated. Besides, the optimum operation conditions are also attained using RSM. Ultimately, the reusability of the magnetic RH is evaluated for estimating its potential and capability at a larger scale.

In this experiment, Ascorbic acid, ferrous sulfate, and ferric chloride were utilized for the magnetization of RH. Ammonium hydroxide (25% v/v) and potassium hydroxide were used as activators. Potassium iodate, potassium iodide, and sulfuric acid were used to prepare the iodine solution. In addition, deionized water was applied as a solvent in all experiments. All used reagents were purchased from Merck Company with high purity (Table 2).

Rice Husk (RH) has been provided from Kozan (Shaft, Guilan, Iran) village farms. The RH has been rinsed with deionized water frequently to eliminate the dust completely. Then, it has been dehydrated in the oven at 90 °C for 24 h until it reaches constant weight, after, turn it into a micro size by the mill. The RH was modified by immersion of 20 g RH into 100 mL of KOH solution at a concentration of 1 M and then stirred for 6 h. The solid was acquired via centrifugation at the rate of 5000 rpm for 10 min. Subsequently, it has been rinsed with deionized water to reach neutral pH. The precipitation method was used to magnetize the RH-KOH. For this aim, 4.1 g of FeCl3 and 2.1 g of FeSO4 have been mixed in 80 mL of deionized water under a certain agitation rate. Afterward, 10 mL of 25% v/v of ammonia solution and a certain dose of RH-KOH were added. The magnetization reaction proceeded for 45 min at 80 °C on a stirrer at 450 rpm. Eventually, the black solid product have been attracted using magnets, rinsed several times with deionized water, and dehydrated at 60 °C for 12 h (Fig. 1). The formula of the magnetic reaction has been brought in Eq. (1).

Schematic for the (a) synthesis of magnetic RH, and (b) chemical structure of synthesis process.

To prepare the standard iodine solution, 0.15 g of potassium iodate (KIO3) was dissolved in a certain amount of deionized water. Then, 3 g of potassium iodide (KI) has been added to the mixture and its volume has been increased to 100 mL. The vessel containing the materials has been mixed using a stirrer to dissolve completely. Afterward, 1 mL of H2SO4 with a concentration of 9 M was gradually introduced into the solution for accelerating the reaction until the appearance of the mixture altered from milky to dark red. Regarding the following reaction, 0.021 M of iodine solution was produced which was made fresh for daily consumption in order to obtain the desired result of the titration process. The reaction of AA with the iodine ions was displayed in Fig. 2.

The reaction between AA and iodine ions during the titration36,37.

The participant functional groups and the variations on the adsorbent before and after the adsorption were performed using Fourier transform infrared spectrophotometer (FTIR) at the wavelength of 400–4000 cm−1 (AVATER, Thermo, USA). The morphological image and compositions of the adsorbent (SEM–EDX) were determined by scanning electron microscopy (Mira3, Tescan, Czech Republic). Fe3O4 composition was characterized by X-ray fluorescence using a diffractometer (Pw1730, Philips, Netherlands) with Cu/Kα radiation (40 kV, 30 mA). Also, a vibrating sample magnetometer (VSM) model of MDKB 4214 was employed for measuring the magnetic property of modified RH. The specific surface area has been identified by applying the Brunauer–Emmett–Teller (BET) equation. The heat stability of the synthesized adsorbents has been investigated by applying the thermogravimetric test (TGA, Model 2960, Universal V2.4F TA Instruments, USA).

The adsorption experiments have been accomplished in the beaker containing 50 mL of AA solution and modified RH. All experiments were performed at room temperature and stirred at 450 rpm, The adsorbent dosage, AA concentrations, temperatures, and contact time were selected in the domain of 0.5–1 g, 400–800 mg/L, 288–308 K, and 10–120 min for finding the best performance conditions of the resin, respectively. After the adsorption process, the resulting suspension was placed in a centrifuge at 3000 rpm for 10 min. The content of the adsorbed AA has been measured using titration with iodine solution in the presence of starch as an indicator. The adsorption process has been repeated in three epochs to reduce the error of the experiment and their mean values were reported. The uptake capacity at the saturation state (qe) and removal efficiency of AA were calculated by the following formulas:

where C0 is the initial concentration of vitamin C (mg/L); Ce is the equilibrium concentration of vitamin C (mg/L); V is the volume of vitamin C solution (L); and W is the dosage of modified RH (g).

Response surface methodology (RSM) is the kind of statistical procedure with the basis of math to obtain the best-predicted models. The aim of this program is to optimize the dependent variable with the help of polynomial equations, which are impacted by independent factors. This technique is popular because it reduces the number of tests, reduces cost and time, and has good precision38. Recently, the use of RSM as a useful method has been expanded compared to the classical method because, in the classical test, the effect of the interaction of the factors on the response is not examined, which causes an error as a result of the experiment. For instance, Chowdhury et al. in 2013 used RSM for optimizing the adsorption of crystal violate with the help of NaOH-modified rice husk. They used design-expert software version 7.1.6. The factors of dye concentration (100–200 mg/L), flow rate (10–30 mL/min), pH, and bed height (5–25 cm). The optimized conditions have obtained pH of 8, concentration of 100 mg/L, flow rate of 22.88 mL/min, and bed height of 18.75 cm39. Popoola in 2019 used a 2-level factorial design for optimizing the experimental conditions such as temperature (600–1000 °C), time (1–5 h), mixing ratio (1–5), and magnetite loading (2–10 wt%) by helping design-expert version 7.0.7. The optimum values of temperature, time, mixing ratio, and magnetite loading were predicted at 859.20 °C, 2.32 h, 2.54, and 5.56 wt%40. In this research, the central composite design (CCD)41 with four autonomic parameters (m = 3) such as acid concentration (XC0 = 400–800 ppm), contact time (Xt = 10–120 min), adsorbent dosage (XD = 0.5–1 g) has been applied for inspecting the separation of AA from the liquid phase. In this experiment, all 3 factors were designed and coded at 5 levels, which are as follows: (− 2, + 2) the lowest and highest level, (− 1, + 1) low and high level, and 0 central points, respectively. Also, The total number of experiments was ordained 20 = 2 m + 2 m + 6 that 16, 8, and 6 are factorial points, axial points (star), and central points, respectively42. The relevance between the response and the factors examined was entailed by a quadratic equation:

Y illustrates the percentage of AA adsorption (predicted response); Xc0, Xt, and XD are autocratic coded factors in the experiment. Furthermore, A0, Ai, Aii, and Aij refer to the coefficients of the linear, quadratic, and interaction between them, respectively, and are random inaccuracy. The significance of the expanded regression models was estimated through the analysis of variance (ANOVA). The design of the experiment for the present adsorption process has been examined using the central composite design (CCD) method under RSM to determine the optimal conditions.

According to Table 3, we define three symbols in the design-expert software such as A, B, and C, which refer to the acid concentration, adsorbent dosage, and contact time, respectively. Also, the value of α was defined at a number of 2 in this software, thus, the central point of the acid concentration, adsorbent dosage, and contact time was calculated at 600, 0.75, and 70, respectively. As can be seen, the number of the levels for these three parameters is 5. The ranges of the experimental parameters were selected with respect to the Refs.43,44,45.

Figure 3 displays the FTIR of the adsorbents for determining the wavelength of the functional moieties in the adsorbent before and after AA adsorption. The peak in the wavelength of 3427 cm−1 was ascribed to the water molecules and the tensile vibrations of the hydroxyl group (–OH) which was due to the intermolecular hydrogen bonding of some reagents like alcohols, phenols, and carboxylic acids in the lignin and cellulose structure. Hydroxyl moieties are on the adsorbent plane. The peak in the wavelength of 2929 cm−1 is attributed to the symmetric and asymmetric tensile vibrations (C–H) of aliphatic acids in cellulose (which is present in the RH structure), which indicates the presence of an alkane functional group (–CH3 or –CH2)46. The peaks in the wavelength of 11,646 cm−1 correspond to asymmetric mobility of (C=O) (carbonyl groups (ketones and aldehydes), carboxylic acid or ester, as well as to tensile vibrations (CN) and flexural vibrations (NH) related to proteins47. The peak is also noted at the wavelengths of 1075 cm−1, and 1646 cm−1, which are attributed to the Si–O–Si tensile vibrations and the asymmetric tensile vibrations of C=O, respectively. Fe–O bonds are vibrating on the surface of the material at the wavelength of 400–600 cm−148,49. As can be seen, after modifying the RH with magnetic iron nanoparticles, a peak with a wavelength of 575–135 cm−1 is formed, which is owing to the mobility of Fe3+ and O2- in the structure of Fe3O450,51. Comparison of Fourier transform infrared spectroscopy before and after adsorption of AA shows that the peaks in the wavelength range of 3427, 2924, and 1646 cm−1 are ascribed to the hydroxyl functional moiety, symmetric and asymmetric tensile vibrations of C–H, and asymmetric (C=O), respectively. The peak is weakened in the wavelength of 1075 cm−1 which is attributed to the Si–O–Si tensile vibrations, which indicates the involvement of these factor groups during the adsorption process. In addition, the peak of Fe–O is amplified after the adsorption process, which can be analyzed in such a way that magnetic iron nanoparticles have participated in the adsorption procedure19,20,52.

The FTIR image of RH, Magnetic RH, Adsorbed AA on the RH, and Adsorbed AA on the Magnetic RH.

SEM test has been performed for studying the morphology of the RH surface before and after AA uptake. The SEM micrograph of the RH shows that the surface has a smooth surface (Fig. 4a) and after the modification, many pores have been dispersed through the RH and its porosity has increased (Fig. 4b). Figure 4c and d also showed the structure of the RH and magnetic RH after the adsorption of AA, respectively. Because of the accumulation of AA molecules, the adsorbent surface became smoother and had fewer depressions, which generally indicates the successful adsorption of AA on the adsorbent surface. The EDX patterns for the detailed study of compounds present in the RH and magnetic RH are displayed in Fig. 4e and f, respectively. This analysis confirms the presence of the iron particles after the modification. The EDX test also implied that the RH contains very small amounts of minerals and carbohydrates such as cellulose and lignin in its structure. Thus, the main elements in the structure of the RH are oxygen, carbon, and a small amount of iron53. Also, Fig. 4f is related to magnetic RH, which, as can be seen from the composition of the percentage, after placing the iron nanoparticles on the RH, the percentage of iron's composition has increased significantly and their carbon and oxygen have diminished, because the nanoparticles are well deposited on the surface of carbon, which is the main constituent of bran54. The main constituents of RH are about 70% of the inorganic part of rice bran, and it is mainly composed of silica and small amounts of alkali metal oxide. RH is composed mainly of lignin (20–30%), holo-cellulose (55–65%), SiO2 (15–20%) and extracts (2–5%), which can be regarded as a natural organic–inorganic composite (Table 4).

The SEM image of (a) RH, (b) Magnetic RH, (c) Adsorbed AA on the RH, and (d) Adsorbed AA on the magnetic RH. The EDX image of (e) RH, and (f) Modified RH. The XPS image of (g) raw, and (h) magnetic RH.

The XPS (X-ray photoelectron spectroscopy) images are illustrated in Fig. 4. The model of the XPS apparatus is SPECS FlexMod. Figure 4g and h show the XPS image of the raw and magnetic RH. In addition, the XPS image after the adsorption is depicted in Fig. 4i. The peaks in Fig. 4g are 285, 533, 400, and 103.50 eV, which relate to the C1s, O1s, N1s, and Si2p, respectively. The peak at the binding energy of 750 eV in Fig. 4h appears which corresponds to the Fe2p because of the presence of the iron elements in the magnetic RH. Figure 4h implies that the magnetization has occurred successfully. According to Fig. 4i, the binding energy of peaks for C1s, O1s, Si2p, and Fe2p has declined which is owing to the chelation of AA to these atoms, and it reveals the successful adsorption of AA onto the magnetic RH. The binding energy of C, O, Si, and Fe after the adsorption of AA are 250, 500, 400, and 95 eV, respectively52.

The X-ray diffraction patterns (Card No. [75-0033 Joint Committee on Magnetic Diffraction Standard (JCPDS)]) for RH and M-KOH-RH adsorbents have been shown in Fig. 5. According to Fig. 5, it is obvious that RH has not a crystalline structure, because of a sharper peak at 2θ of 22.19°, which is ascribed to the existence of organic reagents in the structure of RH (cellulose, hemicellulose, and lignin) and prove the lack of mineral compounds. XRD pattern also reveals the amorphous structure of the RH. The diffraction patterns of Fe3O4 in the modified RH are 30.34, 36.39, 49.43, 53.59, 34.57, 94.62, and 54.74° indicating the presence of magnetic particles on the surface of the RH55,56.

The XRD diagram of RH and magnetic RH.

One of the disadvantages of traditional adsorbents is their separation from the solution, which prevents the adsorbent from reusing. The addition of iron not only increases the adsorption capacity but it can also be conveniently isolated from the adsorbent via employing a magnetic field. Figure 6 shows the magnetic properties of raw and modified RH with a vibrating sample magnetometer (VSM) system. The magnetic field was adjusted in the domain of − 15,000 to + 15,000 Oe at room temperature. Saturation magnetization values for the raw and magnetic RH have been determined at 8 and 57 emu/g, respectively. Regarding Fig. 6, the magnetic property of the raw RH is less than that of the magnetic one, which means that the Fe3O4 particles have occupied the structure of rice successfully.

The VSM diagram of the raw (red line) and magnetic RH (black line).

The BET analysis for the RH and modified RH was conducted. The surface area of the RH and modified RH was determined at 98.17 and 120.23 m2/g, respectively. Besides, the pore volumes of the RH and modified RH have been obtained at 2.10 and 6.20 mm3/g, respectively. It reveals that the modification of RH increases the surface area, which causes improving the adsorption of AA onto the RH due to the increment of pores on the RH. Besides, the TGA analysis of the modified rice husk was performed and it is illustrated in Fig. 7. Regarding this figure, the thermal stability of the modified rice husk was 450℃, which demonstrates the high resistance of the modified rice husk to the temperature elevation.

The TGA diagram of the magnetic RH.

Variance analysis for the adsorption efficiency of AA is conducted by considering the temperature, acid concentration, and dosage in Table 6. In fact, the existence of P-value, F-value, and lack of fit can help us to decide about the significance or insignificance of these parameters. The other case that was brought in this section is predicting an equation for the adsorption process. The equation in terms of actual factors can be used to make predictions about the response for given levels of each factor, thus, defining an appropriate model or equation for the process can help us to describe the behavior of the system better. According to Table 5, different polynomials such as linear, quadratic, and cubic were fitted versus the experimental data in the design-expert software for selecting the closest model to the empirical results. This table reveals that the quadratic polynomial was suggested, thus, the experimental parameters have the degree of two. Equation (6) was also predicted by the software, which explains that there is an optimum point at the center of the quadratic graph instead of the corner points. Besides, this equation should not be used to determine the relative impact of each factor because the coefficients are scaled to accommodate the units of each factor and the intercept is not at the center of the design space. Regarding Table 6, the Predicted R2 of 0.9488 is in reasonable agreement with the Adjusted R2 of 0.9860. Adeq Precision measures the signal-to- noise ratio. A ratio greater than 4 is desirable. The calculated Adeq Precision is 47.553 which indicates an adequate signal. This model can be used to navigate the design space. Regarding Table 7, the P-value of the model has attained lesser than 0.0001 and demonstrated that the models are significant. The F-value for the adsorption percentage is measured at 102.15, which proved the models are significant. There is only a 0.01% possibility that F-values these large could occur because of the noise 57. Regarding Table 6, each model hasn’t lack fit, which proved that the model is appropriate. Regarding Table 6, the P-values of acid concentration, adsorbent dosage, and time have been obtained lesser than 0.0001, which shows the effectiveness of these factors. Table 6 also proves that the interaction between the acid concentration with time, acid concentration with adsorbent dosage, and adsorbent dosage with time are effective on the adsorption efficiency because their P-values are attained at 0.0075, 0.0048, and 0.0064 which are lesser than 0.0558. The model F-value for response is determined 102.15, which indicated the model is significant. There is only 0.01% probability that F-value this large could happen own to noise. In addition, the degree two of the time is effective because its value is 0.0024. According to the RSM results, the optimum experimental conditions have been predicted at the acid concentration of 486.929 ppm, adsorbent dosage of 0.875 g, and time of 105.397 min. In addition, the adsorption efficiency has been obtained at 92.936% at these optimum conditions with the desirability value of 1.00 which is the best value. It is essential to refer to this notice that the values of the acid concentration, adsorbent dosage, and contact time were selected “in range” and the value of response or % R was selected “maximize” in the design-expert software, because our goal was maximizing the adsorption efficiency with respect to the range values of the experimental conditions (Table 8). In Eq. (6), the symbols A, B, and C are ascorbic acid concentration, adsorbent dosage, and contact time, respectively. We have obtained Table 8 by using experiment design software. In this way, we selected the investigated parameters which include the initial concentration, adsorbent dose and contact time by selecting the in range option in the desired range. The purpose of this work is to show values of parameters where R has its maximum value. For this reason, we choose the highest option for R, which is the absorption percentage value, so that the software is able to protect the optimal R value. As shown in the table, in the initial concentration = 718.92 ppm, adsorbent dose = 0.898 mg and contact time = 105 min, we reach the maximum value of absorption percentage which is 92.33%. Also, in the initial concentration = 481 ppm, adsorbent dose = 0.601 mg and contact time = 34 min, we reach the lowest absorption percentage value, which is 25%.

The 3D diagrams induce important information about the impact of three factors on the adsorption efficiency (response) simultaneously by analyzing the effect of interaction between two variables by setting a factor at its central level, which is displayed in Fig. 8. The observations revealed that the interaction of acid concentration and adsorbent dosage on the response was weak (Fig. 8a). As shown in Fig. 8a, the adsorption efficiency dropped mildly with increasing acid concentration, because the number of the penetrated molecules into the active centers increases and can block these centers and there is not an opportunity for the other molecule for filing the vacant cavities. Increasing the adsorbent dosage has a positive impact on the adsorption efficiency, because the number of active sites has been developed and porosity is increased (Fig. 8b,c). Figure 8b and c reveal that the adsorption occurs rapidly at the initial times, because of the presence of more unsaturated active centers at the primary times, and these sites are occupied by the AA with passing time which enhances the mass transfer resistance and the diffusion of the AA molecules is prohibited59,60. The normal probability graph can be utilized to control and survey the normality of the empirical data. The proximity of the squares to the direct line demonstrates the normal dispersion of the error with a mean of zero and a fixed value. According to Fig. 9a, the results of the adsorption efficiency are in the vicinity of the direct line, which reveals the normality of the obtained data of the response. The squares with various colors and straight routes are the experimental and anticipated values, respectively. The more focused the squares are on the straight route proves the better the data distribution. Regarding Fig. 9b, the adsorption percentage of AA placed close to the route displayed that the actual results obeyed a specified function, the data distribution trend was desired and the confidence in the obtained data is high61. The perturbation diagram assists to contrast the influence of all factors at a determined place in the design space. The responses are drawn by varying only one parameter over its limited area while keeping the other parameters unchanged. By default, Design-Expert imagines the criteria placed at the midpoint (coded 0) of the entire parameters. Figure 10 indicated that the change in the adsorption efficiency with each of the effective factors is not a direct route, which proves that the adsorption efficiency of AA is susceptible to variations of entire influential parameters in the adsorption process. Besides, each of the factors has a dissociated point where the response is enlarged. Also, it was derived from Fig. 10, increasing the adsorbent dosage and temperature and decreasing the acid concentrations from the optimized value has a suitable influence on the adsorption process and ultimately the economy of the process61.

The 3D diagram for the effect of the (a) adsorbent dosage and acid concentration, (b) time and acid concentration, and (c) time and adsorbent dosage.

The diagram of (a) % probability vs. externally studentized residuals, and (b) predicted vs. actual values.

Perturbation graph of the influential parameters.

The Box-Cox diagram set the best lambda value for the adsorption process at 2.13, indicating that the data did not need to be modified for further improvement (Fig. 11b). The Pareto diagram is another tool to investigate the significance of independent variables on a response (Fig. 11a). The pareto graph shows how well each variable satisfied the criteria: values near one are good. It is observed that the response is one and demonstrating that the aim of maximizing the adsorption percentage is occurred appropriately20,62,63,64.

The (a) Pareto, and (b) Box–Cox diagrams.

Isotherm study provides important information for scaling up and designing the adsorption process65,66. Adsorption equilibrium studies provide comprehensive information to describe the adsorption of solutes between the sorbent surface and solution, especially at the equilibrium state. Figure 12 reveals the diagram of uptake capacity against the acid concentration. Regarding this figure, the uptake capacity increases by acid concentration in temperatures of 15, 25, and 35 °C. Table 9 shows the factors of the isotherm models for the adsorption of AA on the modified KOH rice husk (M-KOH-RH) at temperatures of 15, 25, and 35℃. In the present work, the empirical results have been fitted with the four isotherm models such as Langmuir, Freundlich, Temkin, and Dubinin–Radushkevich (D–R)67. The equations of four isotherm models are presented below:

The diagram of uptake capacity vs. the acid concentration.

The constants in the Langmuir, Freundlich, and Tamkin relations are KL, KF, and β, respectively. In these equations, qe (mg/g), qm (mg/g), and C0 (mg/L) refer to the saturation uptake capability, maximum adsorbent capacity, and initial adsorbent content. Also, ε is the polarization potential of the D–R equation, the constant K refers to the average free adsorption energy, and the qD (mg/g) refers to the theoretical saturation absorption capability. n is also the heterogeneity coefficient of the Freundlich model. The n parameter for the AA adsorption process using modified rice husk is 10.384 which shows that the adsorption process by these adsorbents is physical and is done easily65. AT (L/min) is an equilibrium connection constant of the Temkin model. Table 9 shows the different parameters of the adsorption isotherm with the linear fitting of four models at temperatures of 15 °C, 25 °C, and 35 °C. By comparing the regression values, it can be concluded that the Langmuir and D–R isotherm models have the most adaption with the experimental data. In the Langmuir model, the loading of AA on the adsorbent plane is monolayer and the tensile strength of all adsorption centers and sites is the same for the adsorbent component, meaning that AA molecules are uniformly located on the plane of the resin. Also, enhancing the temperature enables the increase of the uptake capability. In the Freundlich equation, it is assumed that multilayer penetration occurs on non-homogeneous planes or surfaces with different activity centers and positions in terms of energy and affinity with the adsorbent component. The RL parameter at Langmuir's isotherm [Eq. (4)] indicates the desirability (0 < RL < 1) of the adsorption process of AA by the adsorbent. In Freundlich's isothermal model, Kf increases with increasing temperature. Also, the amount of n higher than unity indicates that the M-KOH-RH adsorbent can be used for all AA concentration ranges. In the Temkin isotherm model, the values of the β parameter also increase with increasing temperature, which means more heat is absorbed. Also, the AT parameter has the highest value in the isothermal isotherm model for the adsorbent at 35 °C, which indicates the adsorbent-adsorption interaction for the adsorbent at this temperature is larger than at the other temperatures. Examining the values of parameter which indicates the average free adsorption energy and the adsorption mechanism in terms of being physical or chemical. If the value of mean free energy is between 8 and 16 kJ/mol, the adsorption process is ion change type. If its value is less than 8 kJ/mol, it shows in adsorption that the mechanism of the adsorption process is physical65. In the D–R model, it is obvious that the physical adsorption mechanism (E > 8) is the dominant mechanism for adsorption68.

In order to imply the physical or chemical mechanism between the resin and solute, the kinetic study of the adsorption is a useful and efficient method. Figure 13 shows the affinity of the adsorption percentage and uptake capacity to the time. According to this figure, the adsorption percentage and the adsorption capacity increase by time enhancement in both raw rice husk and the modified one. The equilibrium time for the rice husk and the modified rice husk has been observed at 120 and 30 min, respectively, which is owing to the penetration of AA between the layers of the adsorbents and AA deposited on the adsorbent surface. In the adsorption process, the active sites of the adsorbent become gradually altered and resulting in reduced adsorption rates69,70. It was concluded the modified rice husk could adsorb the AA rapidly. Adsorption kinetic data were obtained at the AA concentration of 481 ppm, and adsorbent dose of 0.898 mg using well-known kinetic models such as pseudo-first-order, pseudo-second-order, Elovich, and diffusion Intra-particle71. The kinetic equations are written below:

The diagram of (a) the adsorption percentage vs. the time, and (b) uptake capacity vs. the time.

In the above equations, \({\mathrm{q}}_{\mathrm{e }}(\mathrm{mg}/\mathrm{g})\), and \({\mathrm{q}}_{\mathrm{t}}(\mathrm{mg}/\mathrm{g})\) indicate the uptake capability at the saturation state, and at the time of t, respectively. The constants of the pseudo-first-order and pseudo-second-order equations were denoted by \({\mathrm{k}}_{1}\) (1/min) and \({\mathrm{k}}_{2}\) (g/mg min(.

In Eqs. (13) and (14), α and β are the constants of the Elovich model, which are called the adsorption rate (mg/g.min) and the desorption constant (g/mg), respectively. Kp (mg (g min0.5)−1) and C(mg/g) also describe the intra-particle diffusion rate and the boundary layer constant, respectively.

Table 10 shows the various parameters calculated by fitting four kinetic equations. According to Table 10, the pseudo-second-order equation has a more correlation relative to the other kinetic equations, which means that the chemical behavior is dominant in the separation procedure in which the electron sharing occurred between the composite and the solutes and also the intensity of separation of molecules on the adsorbent surface is linear and a function of the number of active sites. The intra-particle diffusion of adsorption took place in two stages, the first stage has a higher R2 and Kp than the second stage, which indicates that the dominant process is the mobility of AA from a liquid phase to the surface of the resin72,73.

Thermodynamics of the separation process has been studied at various heat degrees to detect the impact of temperature on the separation procedure. The initial solution temperature provides the energy needed for the system and affects the system's adsorption capacity. In order to evaluate the behavior of each process in terms of feasibility and spontaneity, its energy functions and entropy should be considered19,21,74. Thermodynamic parameters like Gibbs free energy change (∆G°), enthalpy change (∆H°), and entropy change (∆S°) contribute to interpreting the adsorption performance under several heat degrees. For this aim, the quantities of ∆G°, ∆H°, and ∆S° at 293, 303, and 313 K were obtained as follows and their values have been calculated with respect to Fig. 14:

The diagram of ln(KC) vs. 1/T.

Where KC is the saturation constant, R is the universal gas constant (8.314 kJ/mol K) and T is the absolute temperature (K). The thermodynamic factors of the adsorption have been listed in Table 11. This means that the process of adsorption of AA on the surface of the magnetic sorbent is endothermic, because the sign of ΔH° is positive. Positive values for ΔSo indicate an increase of irregularity in the boundary layer between the solid phase and the liquid phase. Also, a low enthalpy value indicates weak interactions between AA and functional groups present on the adsorbent surface and the adsorption process is physical65. Finally, negative values for the ΔG° parameter mean that the ascorbic acid adsorption process on the solid surface is spontaneous75.

The mechanism for the adsorption of AA on the plane of the treated resin has been drawn in Fig. 15. With respect to this Scheme, electrostatic interactions and functional groups interfered with the adsorption mechanism of AA on the modified RH. The electrostatic interaction exists between the divalent iron ions and C=O in the aromatic ring of the AA and silicate ions of the adsorbent with the hydroxyl groups of the aromatic ring of the AA. In addition, the bond formation between the hydroxyl ions of the modified RH and the C–H of the AA backbone is the participation of the functional moieties in the separation mechanism. Moreover, the intra-particle diffusion equation in the kinetic study proves that the mass transfer mechanism of the AA adsorption divides into two parts including (a) Transportation of the AA particles from the AA solution onto the plane of the modified RH and (b) Penetration of AA molecules inside the channels of the modified RH. This kinetic model also explains that the first step or the first case is rapid. In addition, the separation mechanism of AA particles onto the plane of the resin is associated by releasing heat.

Schematic for the adsorption mechanism.

The comparison between the present work with the other works was collected in Table 12. This Table demonstrates that rice husk and modified rice husk were employed for the adsorption of different toxic components such as dyes, phenol, and metallic ions. According to this Table, both rice husk and modified rice husk have been used more for the adsorption of different dyes, and it was observed no papers about the adsorption of ascorbic acid onto the modified rice husk. Among the examined dyes, methylene blue could be adsorbed onto the modified rice husk (alginate/rice husk) with a higher uptake capacity (274.90 mg/g) relative to the other dyes. Rice husk could also adsorb the synthetic dye with a considerable adsorption percentage which was 99.50%. Besides its good uptake capacity in the adsorption of methylene blue, modified rice husk (KOH/rice husk) could likewise adsorb phenol with a high uptake capacity which was attained at 215.27 mg/g. The ability of adsorption for modified rice husk was relatively low for metallic ions like Mn(II) and Co(II) ions. Since the modified rice husk has exhibited good results in the elimination of dyes, phenol, and metallic ions, the authors decided to evaluate the potential of the modified rice husk (KOH/rice husk) for adsorption of ascorbic acid. Regarding this table, the modified rice husk has shown a dramatic adsorption percentage (92.936%) for ascorbic acid, therefore, KOH/rice husk can be a suitable natural adsorbent for adsorbing the ascorbic acid.

In order to save adsorbents, it is essential to survey the reusability of modified RH during adsorption. The reusability of the sorbents is an important factor in industrial applications. In our research, 0.1 mol/L HCl has been selected for leaching the AA from the modified RH68. In fact, the modified RH with the adsorbed AA molecules was soaked in the vessel containing 0.1 mol/L HCl for 30 min, and then the adsorbent was rinsed with the deionized water 3 times. Subsequently, it was dried in the oven. After this mentioned process, the modified RH was used again for trapping the AA molecules. The results of the desorption prove that the modified RH is a suitable adsorbent for leaching the AA molecules because the adsorption efficiency at the equilibrium point in the initial and the terminal cycle has been detected at 92 mg/g and 89.5 mg/g, respectively (Fig. 16). In other words, the adsorption efficiency of the modified RH decreased % 2.71 only. Hence, the modified RH is advised to use more than five times without a dramatic reduction in the adsorption efficiency, implying that the modified RH is completely reused frequently.

The reusability result for the modified RH at the acid concentration of 486.929 ppm, adsorbent dosage of 0.875 g, and time of 105 min.

In this section, we want to know how the anion and cation alter the adsorption of AA. The results are exhibited in Fig. 17. The cation and anion in this research are Ca2+ and Cl− With respect to Fig. 17, the presence of an anion has a slight impact on the adsorption capacity, and the presence of a cation has almost a considerable effect on the adsorption capacity. The adsorption capacity of AA on the magnetic RH without the presence of cation and anion has been obtained at 92 mg/g. The adsorption capacity of AA on the magnetic RH in the presence of cation and anion has been obtained at 84.3 and 90.5 mg/g, respectively. Since the sorbent has a negative charge and anions have also a negative charge. Therefore, the repulsion electrostatic force is created between the anions and the surface of the adsorbent which has a little impact on the adsorption of AA onto the adsorbent. In addition, when the cations are added to the AA solution, they compete with the AA particles for binding with the functional groups. Besides, cations can bind with the negative sites of the adsorbent surface and the negative charge of the AA structure91.

The effect of anion and cation on the adsorption capacity of the AA using the modified RH at the acid concentration of 486.929 ppm, adsorbent dosage of 0.875 g, and time of 105 min.

In this current research, the RH was modified by adding Fe2O3 to its network for the adsorption of AA from the aqueous solution for the first time. The characterization tests, isotherm, kinetic, thermodynamic modeling, and reusability test have occurred for studying the adsorption potential of the modified RH. Besides the experimental results, the design-expert software version 11 was considered for detecting the optimum experimental conditions in which the adsorption efficiency would be maximized at those conditions. These results have been derived which were written below:

The optimum conditions of the design-expert software have been obtained at 486.929 ppm of acid concentration, 0.875 g of the adsorbent dosage, and 105.397 min of the contact time, and the adsorption efficiency in these conditions was determined at 92.936%.

The reusability test exhibits that the adsorption efficiency at the equilibrium point in the initial and the terminal cycle has been detected at 92 mg/g and 78 mg/g, respectively, which showed the modified RH can be used more than five times without dramatic reduction in the adsorption efficiency.

The surface area of the RH and modified RH was determined at 98.17 and 120.23 m2/g, respectively.

The thermal stability of the modified rice husk was 450 °C.

The Langmuir model had the highest R2 of 0.9982, 0.9996, and 0.9985 at the temperature of 15, 25, and 35 °C, respectively, and also the qmax values in these temperatures have been calculated at 19.157, 31.34, and 38.75 mg/g, respectively.

The pseudo-second-order kinetic model had the best agreement with the experimental results. In this kinetic model, the values of q have been measured at 36.496, 45.248, and 49.019 mg/g at the acid concentration of 418, 600, and 718 ppm, respectively.

The values of ΔH° and ΔS° were measured at 31.972 kJ/mol and 120.253 kJ/mol K, respectively, which proves the endothermic and irregular nature of the adsorption of AA.

Electrostatic interactions and functional groups interfered in the adsorption mechanism of AA on the modified RH.

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

Sikora, M. & Świeca, M. Effect of ascorbic acid postharvest treatment on enzymatic browning, phenolics and antioxidant capacity of stored mung bean sprouts. Food Chem. 239, 1160–1166 (2018).

Article CAS PubMed Google Scholar

Aguirre, M. Á., Long, K. D., Canals, A. & Cunningham, B. T. Point-of-use detection of ascorbic acid using a spectrometric smartphone-based system. Food Chem. 272, 141–147 (2019).

Article CAS PubMed Google Scholar

Igual, M., García-Martínez, E., Camacho, M. & Martínez-Navarrete, N. Effect of thermal treatment and storage on the stability of organic acids and the functional value of grapefruit juice. Food Chem. 118, 291–299 (2010).

Article CAS Google Scholar

Wald, E. L. et al. Hydrocortisone–ascorbic acid–thiamine use associated with lower mortality in pediatric septic shock. Am. J. Respir. Crit. Care Med. 201, 863–867 (2020).

Article PubMed Google Scholar

Fang, T. et al. Variation of ascorbic acid concentration in fruits of cultivated and wild apples. Food Chem. 225, 132–137 (2017).

Article CAS PubMed Google Scholar

Rodríguez, G. M., Sibaja, J. C., Espitia, P. J. & Otoni, C. G. Antioxidant active packaging based on papaya edible films incorporated with Moringa oleifera and ascorbic acid for food preservation. Food Hydrocolloids 103, 105630 (2020).

Article Google Scholar

Mazurek, A. & Jamroz, J. Precision of dehydroascorbic acid quantitation with the use of the subtraction method: Validation of HPLC–DAD method for determination of total vitamin C in food. Food Chem. 173, 543–550 (2015).

Article CAS PubMed Google Scholar

Masoumi, H., Ghaemi, A. & Gilani, H. G. Exploiting the performance of hyper-cross-linked polystyrene for removal of multi-component heavy metal ions from wastewaters. J. Environ. Chem. Eng. 9, 105724 (2021).

Article CAS Google Scholar

Ahmed, M. B. et al. Activated carbon preparation from biomass feedstock: Clean production and carbon dioxide adsorption. J. Clean. Prod. 225, 405–413 (2019).

Article CAS Google Scholar

Franco, D. S. et al. Highly effective adsorption of synthetic phenol effluent by a novel activated carbon prepared from fruit wastes of the Ceiba speciosa forest species. J. Environ. Chem. Eng. 9, 105927 (2021).

Article CAS Google Scholar

Gu, S., Kang, X., Wang, L., Lichtfouse, E. & Wang, C. Clay mineral adsorbents for heavy metal removal from wastewater: A review. Environ. Chem. Lett. 17, 629–654 (2019).

Article CAS Google Scholar

Alavijeh, M. A., Sarvi, M. N. & Afarani, Z. R. Properties of adsorption of vitamin B12 on nanoclay as a versatile carrier. Food Chem. 219, 207–214 (2017).

Article Google Scholar

Ghaemi, A., Torab-Mostaedi, M. & Ghannadi-Maragheh, M. Characterizations of strontium(II) and barium(II) adsorption from aqueous solutions using dolomite powder. J. Hazard. Mater. 190, 916–921 (2011).

Article CAS PubMed Google Scholar

Ghaemi, A., Torab-Mostaedi, M., Shahhosseini, S. & Asadollahzadeh, M. Characterization of Ag(I), Co(II) and Cu(II) removal process from aqueous solutions using dolomite powder. Korean J. Chem. Eng. 30, 172–180 (2013).

Article CAS Google Scholar

Assaf, J. C. et al. Assorted methods for decontamination of aflatoxin M1 in milk using microbial adsorbents. Toxins 11, 304 (2019).

Article CAS PubMed PubMed Central Google Scholar

Ince, O. K., Ince, M., Yonten, V. & Goksu, A. A food waste utilization study for removing lead(II) from drinks. Food Chem. 214, 637–643 (2017).

Article PubMed Google Scholar

Saleh, T. A. Protocols for synthesis of nanomaterials, polymers, and green materials as adsorbents for water treatment technologies. Environ. Technol. Innov. 24, 101821 (2021).

Article CAS Google Scholar

Stuart, P. The Advantages and Disadvantages of Anaerobic Digestion as a Renewable Energy Source (Loughborough University, 2006).

Google Scholar

Foroutan, R., Peighambardoust, S. J., Mohammadi, R., Peighambardoust, S. H. & Ramavandi, B. Development of new magnetic adsorbent of walnut shell ash/starch/Fe3O4 for effective copper ions removal: Treatment of groundwater samples. Chemosphere 296, 133978 (2022).

Article ADS CAS PubMed Google Scholar

Ahmadi, A. et al. Montmorillonite clay/starch/CoFe2O4 nanocomposite as a superior functional material for uptake of cationic dye molecules from water and wastewater. Mater. Chem. Phys. 284, 126088 (2022).

Article CAS Google Scholar

Foroutan, R. et al. Nickel ions abatement from aqueous solutions and shipbuilding industry wastewater using ZIF-8-chicken beak hydroxyapatite. J. Mol. Liq. 356, 119003 (2022).

Article CAS Google Scholar

Savari, A. et al. Physicochemical characteristics and mechanism of fluoride removal using powdered zeolite-zirconium in modes of pulsed & continuous sonication and stirring. Adv. Powder Technol. 31, 3521–3532 (2020).

Article CAS Google Scholar

Khoshraftar, Z., Masoumi, H. & Ghaemi, A. An insight into the potential of dolomite powder as a sorbent in the elimination of heavy metals: A review. Case Stud. Chem. Environ. Eng. 7, 100276 (2022).

Article Google Scholar

Masoumi, H., Ghaemi, A. & Gilani, H. G. Evaluation of hyper-cross-linked polymers performances in the removal of hazardous heavy metal ions: A review. Separation Purif. Technol. 260, 118221 (2020).

Article Google Scholar

Ruthiraan, M. et al. An overview of magnetic material: Preparation and adsorption removal of heavy metals from wastewater. Magn. Nanostruct. Environm. Agric. Appl. 1, 131–159 (2019).

Article Google Scholar

Homagai, P. L., Poudel, R., Poudel, S. & Bhattarai, A. Adsorption and removal of crystal violet dye from aqueous solution by modified rice husk. Heliyon 8, e09261 (2022).

Article CAS PubMed PubMed Central Google Scholar

Bansal, M., Garg, U., Singh, D. & Garg, V. Removal of Cr (VI) from aqueous solutions using pre-consumer processing agricultural waste: A case study of rice husk. J. Hazard. Mater. 162, 312–320 (2009).

Article CAS PubMed Google Scholar

Chowdhury, S., Mishra, R., Saha, P. & Kushwaha, P. Adsorption thermodynamics, kinetics and isosteric heat of adsorption of malachite green onto chemically modified rice husk. Desalination 265, 159–168 (2011).

Article CAS Google Scholar

El-Shafey, E. Sorption of Cd(II) and Se(IV) from aqueous solution using modified rice husk. J. Hazard. Mater. 147, 546–555 (2007).

Article CAS PubMed Google Scholar

Hsu, S.-T. & Pan, T.-C. Adsorption of paraquat using methacrylic acid-modified rice husk. Biores. Technol. 98, 3617–3621 (2007).

Article CAS Google Scholar

Chen, Y., Wang, F., Duan, L., Yang, H. & Gao, J. Tetracycline adsorption onto rice husk ash, an agricultural waste: Its kinetic and thermodynamic studies. J. Mol. Liq. 222, 487–494 (2016).

Article CAS Google Scholar

Ashrafi, S. D., Kamani, H., Jaafari, J. & Mahvi, A. H. Experimental design and response surface modeling for optimization of fluoroquinolone removal from aqueous solution by NaOH-modified rice husk. Desalin. Water Treat. 57, 16456–16465 (2016).

Article CAS Google Scholar

Fatima, T., Nadeem, R., Masood, A., Saeed, R. & Ashraf, M. Sorption of lead by chemically modified rice bran. Int. J. Environ. Sci. Technol. 10, 1255–1264 (2013).

Article CAS Google Scholar

Lahieb, F. M., Al-Sharify, Z. T., Farah, F. M. Role of rice husk as natural sorbent in paracetamol sorption equilibrium and kinetics. In: IOP Conference Series: Materials Science and Engineering, 012053. (IOP Publishing, 2020).

Awwad, N., Gad, H., Ahmad, M. & Aly, H. Sorption of lanthanum and erbium from aqueous solution by activated carbon prepared from rice husk. Colloids Surf. B 81, 593–599 (2010).

Article CAS Google Scholar

Suntornsuk, L., Gritsanapun, W., Nilkamhank, S. & Paochom, A. Quantitation of vitamin C content in herbal juice using direct titration. J. Pharm. Biomed. Anal. 28, 849–855 (2002).

Article CAS PubMed Google Scholar

Munir, N., Hameed, A., Haq, R. & Naz, S. Biochemical changes in cultivars of sweet oranges infected with citrus tristeza virus. Braz. J. Biol. 79, 742–748 (2019).

Article CAS PubMed Google Scholar

Wu, W. et al. Preparation process optimization of pig bone collagen peptide-calcium chelate using response surface methodology and its structural characterization and stability analysis. Food Chem. 284, 80–89 (2019).

Article CAS PubMed Google Scholar

Chowdhury, S., Chakraborty, S. & Saha, P. D. Response surface optimization of a dynamic dye adsorption process: A case study of crystal violet adsorption onto NaOH-modified rice husk. Environ. Sci. Pollut. Res. 20, 1698–1705 (2013).

Article CAS Google Scholar

Popoola, L. T. Nano-magnetic walnut shell-rice husk for Cd(II) sorption: Design and optimization using artificial intelligence and design expert. Heliyon 5, e02381 (2019).

Article PubMed PubMed Central Google Scholar

Bhattacharya, S. Central composite design for response surface methodology and its application in pharmacy. In Response surface Methodology in Engineering Science (IntechOpen, 2021).

De Oliveira, L. G. et al. Response surface methodology for advanced manufacturing technology optimization: Theoretical fundamentals, practical guidelines, and survey literature review. Int. J. Adv. Manuf. Technol. 104, 1785–1837 (2019).

Article Google Scholar

Zhang, P. et al. A green biochar/iron oxide composite for methylene blue removal. J. Hazard. Mater. 384, 121286 (2020).

Article CAS PubMed Google Scholar

Ooi, J. et al. Assessment of fish scales waste as a low cost and eco-friendly adsorbent for removal of an azo dye: Equilibrium, kinetic and thermodynamic studies. Biores. Technol. 245, 656–664 (2017).

Article CAS Google Scholar

Munagapati, V. S., Wen, J.-C., Pan, C.-L., Gutha, Y. & Wen, J.-H. Enhanced adsorption performance of reactive red 120 azo dye from aqueous solution using quaternary amine modified orange peel powder. J. Mol. Liq. 285, 375–385 (2019).

Article CAS Google Scholar

Daffalla, S. B., Mukhtar, H. & Shaharun, M. S. Characterization of adsorbent developed from rice husk: Effect of surface functional group on phenol adsorption. J. Appl. Sci. 10, 1060 (2010).

Article ADS CAS Google Scholar

Katal, R., Baei, M. S., Rahmati, H. T. & Esfandian, H. Kinetic, isotherm and thermodynamic study of nitrate adsorption from aqueous solution using modified rice husk. J. Ind. Eng. Chem. 18, 295–302 (2012).

Article CAS Google Scholar

Emdadi, Z., Asim, N., Yarmo, M. A. & Sopian, K. Effect of chemical treatments on rice husk (RH) water absorption property. Int. J. Chem. Eng. Appl. 6, 273 (2015).

CAS Google Scholar

Shen, Y. & Fu, Y. KOH-activated rice husk char via CO2 pyrolysis for phenol adsorption. Mater. Today Energy 9, 397–405 (2018).

Article Google Scholar

Wen, T. et al. Production of a generic magnetic Fe3O4 nanoparticles decorated tea waste composites for highly efficient sorption of Cu(II) and Zn(II). J. Environ. Chem. Eng. 5, 3656–3666 (2017).

Article CAS Google Scholar

Chang, J. et al. Adsorption of methylene blue onto Fe3O4/activated montmorillonite nanocomposite. Appl. Clay Sci. 119, 132–140 (2016).

Article CAS Google Scholar

Gong, J. et al. Shellac-coated iron oxide nanoparticles for removal of cadmium(II) ions from aqueous solution. J. Environ. Sci. 24, 1165–1173 (2012).

Article CAS Google Scholar

Shoumkova, A. & Stoyanova, V. SEM–EDX and XRD characterization of zeolite NaA, synthesized from rice husk and aluminium scrap by different procedures for preparation of the initial hydrogel. J. Porous Mater. 20, 249–255 (2013).

Article CAS Google Scholar

Yuwei, C. & Jianlong, W. Preparation and characterization of magnetic chitosan nanoparticles and its application for Cu(II) removal. Chem. Eng. J. 168, 286–292 (2011).

Article Google Scholar

Liu, X. et al. Enhanced dyes adsorption from wastewater via Fe3O4 nanoparticles functionalized activated carbon. J. Hazard. Mater. 373, 397–407 (2019).

Article CAS PubMed Google Scholar

Zhu, H.-Y. et al. Adsorption removal of congo red onto magnetic cellulose/Fe3O4/activated carbon composite: Equilibrium, kinetic and thermodynamic studies. Chem. Eng. J. 173, 494–502 (2011).

Article CAS Google Scholar

Fox, J. & Weisberg, S. Visualizing fit and lack of fit in complex regression models with predictor effect plots and partial residuals. J. Stat. Softw. 87, 1–27 (2018).

Article Google Scholar

Khoshraftar, Z., Masoumi, H. & Ghaemi, A. Experimental, response surface methodology (RSM) and mass transfer modeling of heavy metals elimination using dolomite powder as an economical adsorbent. Case Stud. Chem. Environ. Eng. 7, 100329 (2023).

Article CAS Google Scholar

Azimi, E. B., Badiei, A. & Ghasemi, J. B. Efficient removal of malachite green from wastewater by using boron-doped mesoporous carbon nitride. Appl. Surf. Sci. 469, 236–245 (2019).

Article ADS Google Scholar

Asfaram, A., Ghaedi, M., Hajati, S. & Goudarzi, A. Synthesis of magnetic γ-Fe2O3-based nanomaterial for ultrasonic assisted dyes adsorption: modeling and optimization. Ultrason. Sonochem. 32, 418–431 (2016).

Article CAS PubMed Google Scholar

Masoumi, H., Ghaemi, A. & Ghanadzadeh, H. G. Elimination of lead from multi-component lead-nickel-cadmium solution using hyper-cross-linked polystyrene: Experimental and RSM modeling. J. Environ. Chem. Eng. 9, 106579 (2021).

Article CAS Google Scholar

Foroutan, R., Peighambardoust, S. J., Mohammadi, R., Ramavandi, B. & Boffito, D. C. One-pot transesterification of non-edible Moringa oleifera oil over a MgO/K2CO3/HAp catalyst derived from poultry skeletal waste. Environ. Technol. Innov. 21, 101250 (2021).

Article CAS Google Scholar

Foroutan, R., Peighambardoust, S. J., Mohammadi, R., Peighambardoust, S. H. & Ramavandi, B. Application of walnut shell ash/ZnO/K2CO3 as a new composite catalyst for biodiesel generation from Moringa oleifera oil. Fuel 311, 122624 (2022).

Article CAS Google Scholar

Foroutan, R., Peighambardoust, S. J., Mohammadi, R., Peighambardoust, S. H. & Ramavandi, B. Application of waste chalk/CoFe2O4/K2CO3 composite as a reclaimable catalyst for biodiesel generation from sunflower oil. Chemosphere 289, 133226 (2022).

Article ADS CAS PubMed Google Scholar

Foroutan, R., Zareipour, R. & Mohammadi, R. Fast adsorption of chromium (VI) ions from synthetic sewage using bentonite and bentonite/bio-coal composite: A comparative study. Mater. Res. Express 6, 025508 (2018).

Article ADS Google Scholar

Khatooni, H., Peighambardoust, S. J., Foroutan, R., Mohammadi, R. & Ramavandi, B. Adsorption of methylene blue using sodium carboxymethyl cellulose-g-poly (acrylamide-co-methacrylic acid)/Cloisite 30B nanocomposite hydrogel. J. Polym. Environ. 31, 297–311 (2023).

Article CAS Google Scholar

Masoumi, H., Ghaemi, A. & Gilani, H. G. Evaluation of hyper-cross-linked polymers performances in the removal of hazardous heavy metal ions: A review. Sep. Purif. Technol. 260, 118221 (2020).

Article Google Scholar

Li, Y. et al. Preparation of magnetic mesoporous silica from rice husk for aflatoxin B1 removal: Optimum process and adsorption mechanism. PLoS ONE 15, e0238837 (2020).

Article CAS PubMed PubMed Central Google Scholar

Noori, M., Tahmasebpoor, M. & Foroutan, R. Enhanced adsorption capacity of low-cost magnetic clinoptilolite powders/beads for the effective removal of methylene blue: Adsorption and desorption studies. Mater. Chem. Phys. 278, 125655 (2022).

Article CAS Google Scholar

Naeimi, B., Foroutan, R., Ahmadi, B., Sadeghzadeh, F. & Ramavandi, B. Pb(II) and Cd(II) removal from aqueous solution, shipyard wastewater, and landfill leachate by modified Rhizopus oryzae biomass. Mater. Res. Express 5, 045501 (2018).

Article ADS Google Scholar

Zhou, Y. et al. Removal of aflatoxin B1 from aqueous solution using amino-grafted magnetic mesoporous silica prepared from rice husk. Food Chem. 389, 132987 (2022).

Article PubMed Google Scholar

Lawagon, C. P., Amon, R. E. C., Lawagon, C. P. & Amon, R. E. C. Magnetic rice husk ash’cleanser’as efficient methylene blue adsorbent. Environ. Eng. Res. 25, 685–692 (2019).

Article Google Scholar

Ruiz, B. G., Roux, S., Courtois, F. & Bonazzi, C. Spectrophotometric method for fast quantification of ascorbic acid and dehydroascorbic acid in simple matrix for kinetics measurements. Food Chem. 211, 583–589 (2016).

Article Google Scholar

Hosseini, S. S., Hamadi, A., Foroutan, R., Peighambardoust, S. J. & Ramavandi, B. Decontamination of Cd2+ and Pb2+ from aqueous solution using a magnetic nanocomposite of eggshell/starch/Fe3O4. J. Water Process Eng. 48, 102911 (2022).

Article Google Scholar

Andrade, C. A. et al. Adsorption behavior and mechanism of oxytetracycline on rice husk ash: kinetics, equilibrium, and thermodynamics of the process. Water Air Soil Pollut. 231, 1–16 (2020).

Article Google Scholar

Chen, S. et al. Study on the adsorption of dyestuffs with different properties by sludge-rice husk biochar: Adsorption capacity, isotherm, kinetic, thermodynamics and mechanism. J. Mol. Liq. 285, 62–74 (2019).

Article CAS Google Scholar

Kheddo, A., Rhyman, L., Elzagheid, M. I., Jeetah, P. & Ramasami, P. Adsorption of synthetic dyed wastewater using activated carbon from rice husk. SN Appl. Sci. 2, 1–14 (2020).

Article Google Scholar

Alver, E., Metin, A. Ü. & Brouers, F. Methylene blue adsorption on magnetic alginate/rice husk bio-composite. Int. J. Biol. Macromol. 154, 104–113 (2020).

Article CAS PubMed Google Scholar

Tavlieva, M. P., Genieva, S. D., Georgieva, V. G. & Vlaev, L. T. Thermodynamics and kinetics of the removal of manganese(II) ions from aqueous solutions by white rice husk ash. J. Mol. Liq. 211, 938–947 (2015).

Article CAS Google Scholar

Anbia, M., Parvin, Z. & Sepehrian, M. Application of modified nanoporous materials in ascorbic acid adsorption. Part. Sci. Technol. 37, 750–756 (2018).

Article Google Scholar

Lv, S., Li, C., Mi, J. & Meng, H. A functional activated carbon for efficient adsorption of phenol derived from pyrolysis of rice husk, KOH-activation and EDTA-4Na-modification. Appl. Surf. Sci. 510, 145425 (2020).

Article CAS Google Scholar

Suc, N. V. & Kim Chi, D. Removal of rhodamine B from aqueous solution via adsorption onto microwave-activated rice husk ash. J. Dispers. Sci. Technol. 38, 216–222 (2017).

Article CAS Google Scholar

Ashrafi, S., Kamani, H. & Mahvi, A. The optimization study of direct red 81 and methylene blue adsorption on NaOH-modified rice husk. Desalin. Water Treat. 57, 738–746 (2016).

Article CAS Google Scholar

Franco, D. S., Cunha, J. M., Dortzbacher, G. F. & Dotto, G. L. Adsorption of Co (II) from aqueous solutions onto rice husk modified by ultrasound assisted and supercritical technologies. Process Saf. Environ. Prot. 109, 55–62 (2017).

Article CAS Google Scholar

Zhang, G., Qu, J., Liu, H., Cooper, A. T. & Wu, R. CuFe2O4/activated carbon composite: A novel magnetic adsorbent for the removal of acid orange II and catalytic regeneration. Chemosphere 68, 1058–1066 (2007).

Article ADS CAS PubMed Google Scholar

Mathurasa, L. & Damrongsiri, S. Low cost and easy rice husk modification to efficiently enhance ammonium and nitrate adsorption. Int. J. Recycl. Org. Waste Agric. 7, 143–151 (2018).

Article Google Scholar

Saremi, F., Miroliaei, M. R., Nejad, M. S. & Sheibani, H. Adsorption of tetracycline antibiotic from aqueous solutions onto vitamin B6-upgraded biochar derived from date palm leaves. J. Mol. Liq. 318, 114126 (2020).

Article CAS Google Scholar

Kaur, P., Kaur, P. & Kaur, K. Adsorptive removal of imazethapyr and imazamox from aqueous solution using modified rice husk. J. Clean. Prod. 244, 118699 (2020).

Article CAS Google Scholar

Kaykioğlu, G. & Güneş, E. Kinetic and equilibrium study of methylene blue adsorption using H2SO4-activated rice husk ash. Desalin. Water Treat. 57, 7085–7097 (2016).

Article Google Scholar

Mohammadi, M., Ghaemi, A., Torab-Mostaedi, M., Asadollahzadeh, M. & Hemmati, A. Adsorption of cadmium(II) and nickel(II) on dolomite powder. Desalin. Water Treat. 53, 149–157 (2015).

Article CAS Google Scholar

Bui, T. X. & Choi, H. Influence of ionic strength, anions, cations, and natural organic matter on the adsorption of pharmaceuticals to silica. Chemosphere 80, 681–686 (2010).

Article ADS CAS PubMed Google Scholar

Download references

This research did not receive any specific grant from funding agencies in the public, commercial, or not-for-profit sectors.

Department of Chemical Engineering, University of Guilan, Rasht, 4199613776, Iran

Azam Aslani & Hossein Ghanadzadeh Gilani

School of Chemical, Petroleum and Gas Engineering, Iran University of Science and Technology, Tehran, 13114-16846, Iran

Hadiseh Masoumi & Ahad Ghaemi

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

A.A. and H.M.: Conceptualization, Methodology, Software, Conceived and designed the experiments, Validation, Formal analysis, Investigation, Resources, Data curation, Writing—original draft, Writing—review & editing.A.G. and H.G.G.: Supervision, Funding acquisition, Methodology, Software, Validation, Formal analysis, Investigation, Resources, Data curation, Writing—review & editing, Visualization, Project administrationAll authors reviewed the manuscript.

Correspondence to Ahad Ghaemi.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Aslani, A., Masoumi, H., Ghanadzadeh Gilani, H. et al. Improving adsorption performance of l-ascorbic acid from aqueous solution using magnetic rice husk as an adsorbent: experimental and RSM modeling. Sci Rep 13, 10860 (2023). https://doi.org/10.1038/s41598-023-38093-x

Download citation

Received: 11 May 2023

Accepted: 03 July 2023

Published: 05 July 2023

DOI: https://doi.org/10.1038/s41598-023-38093-x

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.