The effect of cobalt/copper ions on the structural, thermal, optical, and emission properties of erbium zinc lead borate glasses

Scientific Reports volume 13, Article number: 12260 (2023) Cite this article

209 Accesses

Metrics details

A host glass network of 70B2O3–10Pb3O4–18ZnO–2Er2O3 (ErCoCu1) was proposed and the impact of 1 mol% of Co or/and Cu ions on its structural, thermal, optical, and green emission properties was studied extensively. The X-ray diffraction spectra confirmed the amorphous structure of the produced glasses. Density and density-based parameters behavior showed that the Co or/and Cu ions fill the interstitial positions of the proposed ErCoCu1 network, causing its compactness. Both ATR-FTIR and Raman Spectra affirmed the formation of the fundamental structural units of the borate network, B–O–B linkage, BO3, and BO4. Additionally, the penetration of Co or/and Cu ions inside the ErCoCu1 converts the tetrahedral BO4 units to triangle BO3 causing its richness by non-bridging oxygens. The addition of Co or/and Cu reduces the glass transition temperature as a result of the conversion of the BO4 to BO3 units. Optical absorption spectra for the host glass ErCoCu1 showed many of the distinguished absorption bands of the Er3+ ion. Penetration of Co ion generates two broadbands referring to the presence of Co2+ ions in both tetrahedral and octahedral coordination and Co3+ ions in the tetrahedral coordination. In the Cu-doped glasses, the characteristic absorption bands of Cu2+ and Cu+ were observed. A green emission was generated from the ErCoCu1 glass under 380 nm excitation wavelength. Moreover, no significant effect of Co or/and Cu on the emission spectra was recorded. The considered glasses had appropriate properties qualifying them for optoelectronics and nonlinear optics applications.

The multiple oxidation states of the transition metal ions TMIs rich the glasses networks by many optical, electrical, and magnetic properties1,2,3. Optically, the TMIs give various specular colors to the glass networks, making them have a high optical absorption ability in the different regions of the electromagnetic spectrum such as UV, visible, and IR regions4,5,6. From the photoluminescence point of view, TMIs generate broad emission bands that have an adjustable wavelength and appropriate quantum yield7,8. Electrically and magnetically, the multiple oxidation states of the TMIs bring substantial modifications in the glass networks structural units by influencing the charge degree of freedom and spin, which in turn directly affect the conduction process and the electrical and magnetic nature of the glass network9,10. Hence, glass-containing TMIs have significant applications in photonics, electronic, optoelectronics, and magnetic domains such as light emitting diodes, optical filters, solid-state lasers, memory-switching electronics, superionic batteries, catalysis, smart electronic devices, and magnetic information storage11,12,13. Cobalt (Co2+/Co3+) and copper (Cu+/Cu2+) ions are of the most distinctive transition metal ions in enhancing the properties of various glass networks. The formation of the mixed valence states of cobalt ions (Co2+/Co3+) in octahedral (oh) and tetrahedral (Td) geometric forms inside the glass network makes it a favorable material in solar selective absorbers, fuel cells, visible and NIR-lasing materials, supercapacitors, gas sensors, and lithium-ion batteries. Cobalt imparts a blue or pink color to the glass depending on the Co2+ ion geometrical shape coordination (tetrahedral or octahedral) 14,15,16. Adding Cu ions to glasses networks generates two valence states, Cu+ and Cu2+, during the preparation process under normal conditions. Cu ions usually add a blue or green color to the glass network. In general, the formation of divalent copper ion Cu2+ can be determined based on the formed color in the glass. In addition, the Cu2+ ion form a broad absorption band in the visible-near infrared range that usually arises due to the octahedral coordination of Cu2+, while the cuprous (monovalent copper) ion Cu+ has a distinct absorption band in the UV region. These absorption bands are usually used to detect the presence of Cu+ and Cu2+ within the glass network1,3,4,7. Rare earth ions RE3+ possess unique properties, the foremost of which is the property of photoluminescence, which made them dominant in many photonics and optoelectronics applications17,18. Er3+ ion is among the rare earth ions that is characterized by its richness in energy levels, which made it a unique light emitter for various spectrum regions such as blue, green, red, and white light17,18. Borate glass is one of the most common glasses networks due to its high transparency and high thermal stability, in addition to its low melting point, which makes the ease its fabrication process. However, due to its high phonon energy, which affects negatively the quantum yield of the photoluminescence, borate glass is reinforced with heavy metal oxides such as PbO and Bi2O319,20. On the other hand, the addition of PbO enhances the mechanical, thermal, and optical properties of the borate glass network19,20. Generally, the borate glass network, especially those reinforced with heavy metal ions is a unique host for all glass additives such as alkali ions (Li+, Na+, etc.), alkaline earth ions (Sr2+, Ba2+, etc.), transition metal ions (Zn2+, Co2+/Co3+, Cu+/Cu2+, etc.), post-transition metal ions (Al3+, Bi3+, etc.), and rare-earth ions (Er3+, Yb3+, etc.)21,22. In view of its aforementioned unique features and the multiplicity of properties that they give to glass networks depending on the concentration, type of glass network, and method of preparation, the studies continue to explore the effective role of transition metal ions in enhancing the glass properties to improve its technological performance in various fields. In 2023, O.I. Sallam et al. studied the impact of four of transition metal ions (CuO, CoO, Fe2O3, and NiO) on the photoluminescence (PL) and dielectric properties of the 20NaF–60P2O5–20Na2O. The authors found that adding CuO and Fe2O3 improves the dielectric parameters of their considered glass, while CoO and NiO reduce the ac conductivity. Their base glass generates emission bands at 480 and 530 nm through pumped them by excitation wavelength of 457 nm. The emission bands position and intensity strongly depended on the type of transition metal dopant1. Kun Lei et al. prepared in 2023 the base glass Na2O–B2O3–SiO2 by ion exchange and studied the influence of Cu+ ions on its structural and luminescence properties. A blue-green broadband centered at 468 nm was generated under 290 nm excitation wavelength and its intensity varied with increasing the ion exchange time7.

Hence and based on the foregoing, the host glass 70B2O3–10Pb3O4–18ZnO–2Er2O3 was inlaid by 1 mol% of Co or/and Cu ions (as an additive not by replacement). The structural changes as a result of the variation of Co or/and Cu ions were studied through X-ray diffraction (XRD) spectra, density and density-based parameters, Attenuated Total Reflectance-Fourier Transform Infrared (ATR-FTIR) spectra, and Raman spectra. Thermally, the glass transition temperature was measured using the Differential Scanning Calorimeter (DSC). In the optical absorption region 200–1600 nm, the optical properties of the considered glasses were studied. Finally; under the influence of the 380 nm excitation wavelength, the photoluminescence spectra in the spectral region of 380–800 nm were recorded.

A host glass network of a chemical composition of 70B2O3–10Pb3O4–18ZnO–2Er2O3 was prepared by the melt/annealing method. After that, two of the transition metal oxides, Co2O3 and CuO, were doped (as an additive not by replacement) with different concentrations as shown in Table 1 to study their impact on the structural, thermal, optical, and photoluminescence properties. Pure raw materials of H3BO3, Pb3O4, ZnO, Er2O3, Co2O3, and CuO were mixed in a porcelain mortar and ground well to reach a uniform color homogeneous powder. Then, the glass was melted at 1100 °C for 1 h in a porcelain crucible to obtain a homogeneous and bubbles-free molten. The molten was then poured for annealing at 300 °C in a steel mold for 30 min.

First, the formation of the amorphous phase of the prepared materials was tested by X-ray diffraction (XRD) patterns. A Philips X-ray diffractometer using a monochromatic Cu-Kα radiation of wavelength 1.54056 Å was used to record the X-ray diffraction spectra. Density and density-based parameters effectively explore the impact of the additives on the physical properties of glass networks, so the density \(\rho \) was measured using Archimedes' principle according to Eq. 13,9,23,24 then density-based parameters (molar volume \({V}_{m}\), mean boron-boron separation \({d}_{B-B}\), oxygen packing density \(OPD\), and packing density \(PD\)) were deduced using the Eqs. 23,9,25,26,27, 312,28, 412,26, and 526.

where \({W}_{a}\) & \({W}_{l}\), \({\rho }_{l}\), \(M\), \({N}_{A}\), \({V}_{m}^{B}\), \(n\), \({x}_{i}\), and \({V}_{i}\) are weight of the sample in air & liquid, the liquid density, the molar mass of the glass sample, the Avogadro’s number, the volume containing 1 mol of boron ions inside the studied glass network, the oxygen atoms number per formula unit, the mole fraction, and the packing factor

The values of the volume containing one mol of boron \({V}_{m}^{B}\) and packing factor \({V}_{i}\) of the ith oxide with a chemical formula \({A}_{b}{O}_{c}\) were calculated using

where \({X}_{B}\), and \({r}_{A}\) & \({r}_{B}\) are the molar fraction of B2O3 and the ionic radii of the cation & the anion.

Attenuated Total Reflection-Fourier Transform Infrared Spectroscopy (ATR-FTIR), (Alpha-Bruker) was used to study the functional groups of the studied glasses in the spectral range of 400–4000 cm−1. Gaussian deconvolution was conducted to pry the origin of the formed broadbands in the ATR-FTIR spectra. The formed tetrahedral BO4 (\({N}_{4}\)) and trigonal BO3 (\({N}_{3}\)) units ratios inside the considered glass network were calculated using Eqs. 6 and 726.

Raman spectra were recorded for the considered glasses by SENTERRA Dispersive Raman Microscope (Bruker) equipped with a diode Nd:YAG laser in the spectral region of 500–4000 cm−1. A narrow-spectrum 532 nm laser excitation system was used to illuminate the produced glasses. Also as the same as of ATR-FTIR, a Gaussian deconvolution to resolve the formed broadbands in the Raman spectra was carried out.

The glass transition temperature of the considered glasses was deduced through a Differential Scanning Calorimeter test using a Mettler–Toledo Instruments, at a 5 °C/min heating rate.

UV–VIS-NIR absorption spectra were measured using a JASCO V-670 UV/Vis spectrophotometer in the spectral region of 200–1600 nm with a 2 nm resolution. Smooth and flat glass samples with dimensions 2 cm2 and thicknesses 1.1–1.4 mm were used in the optical spectra measurements. To determine the existence of various oxidation states of both Co and Cu ions in different geometrical shapes (octahedral and tetrahedral coordination), a deconvolution of the optical absorption spectra was conducted. Based on the obtained absorption bands of Co ions, the ligand field parameters around Co ion; crystal field splitting coefficient 10Dq, Racah parameters B&C, and nephelauxetic ratio β were estimated through the following relations24,25,29.

where \({B}_{free ion}\) of Co is 1120 and \({\nu }_{2}\) and \({\nu }_{3}\) pointed to the bands corresponding to the energy of electronic transitions in tetrahedral Co2+ ions, \({\nu }_{2}\) is the electronic transition corresponding to the visible region and \({\nu }_{3}\) is that to the NIR region.

Based on the optical absorption spectra, the optical band gap of the considered glasses was deduced according to Mott-Davis theory using the following equation9,10,14,24.

where \(\alpha \), \(h\nu \), \(B\), \({E}_{opt}\) are the absorption coefficient, the incident photon energy, the band tailing parameter, and the optical band gap energy respectively. The \(n\) signifies the kind of the occurred electronic transition and take values 1/3 & 1/2 for direct transitions and 2 & 3 for indirect ones. Generally, for glassy materials, the indirect allowed transition is the dominant; hence, the \({E}_{opt}\) values were deduced for the \(n=2\) only. The value of \({E}_{opt}\) estimated through plot the Tauc relation between \(h\nu \) and \({(\alpha h\nu )}^{0.5}\) and by extrapolating the linear part of the curve at \({(\alpha h\nu )}^{0.5}=0\).

To measure the disorder degree in the considered glasses, the band tail, which known as Urbach energy \(\Delta E\) was estimated through the following equation9,10,14,24.

where β is a constant.

The value of Urbach energy determine through the inclination of the linear regions of \(ln\alpha -h\nu \) relation and taking its reciprocal.

The steepness coefficient S, which measures the width of the band-tail in the main gap, was calculated using the formula28,29.

where \(\beta \), \({K}_{B}\), and \(T\) are the exponential constant, Boltzmann constant, and room temperature.

Based on some mathematical contractions, the values of the steepness coefficient can be obtained through a simple relationship that links the steepness coefficient with Urbach energy, which is

Depending on the band gap values, the conducting behavior of the solid (conductor, semiconductor, or insulator) can be characterized. Metallization criterion (M), which is calculated from Eq. 16, is used to determine the conducting behavior of the solid precisely. According to Herzfeld's theory of metallization of the condensed matter, the M value may be approached to zero, close to one, or stands between them, which reflects the conductive, insulating, or semiconducting nature of the solid respectively28,29.

Agilent—Cary eclipse fluorescence spectrophotometer equipped with Xe-lamp was used to record the emission spectra in the spectral region of 380–800 nm. The considered glasses were excited using 380 nm excitation wavelength.

The X-ray diffraction spectra, which are displayed in Fig. 1 signify the amorphicity phase formation of the prepared materials, where, as observed, a broad halo in the spectral range of 22–31° has appeared. It is known that the borate glass forms a broad halo in the spectral range \(2\theta =25{-}30\)°30,31. So, the observed widening in the formed X-ray diffraction peak for the proposed host network, which extended from 22° to 31° arose as a result of the role of Pb3O4, ZnO, and Er2O3 in the network formation. No significant shift in the formed broad halo was observed with the inclusion of Co or/and Cu ions, due to they are being added in small concentrations.

X-ray diffraction patterns of the produced ErCoCu glasses.

Table 2 displays the variation of density and density-based parameters, molar volume \({V}_{m}\), mean boron-boron separation \({d}_{B-B}\), oxygen packing density \(OPD\), and packing density \(PD\), as a result of the penetration of Co or/and Cu ions. First and in general, a weak augmentation in the density and reduction in molar volume with the inlying of Co or/and Cu ions compared to the host glass ErCoCu1 was observed as listed in Table 2. The density augmentation resulted from the fact that the two suggested transition metal ions, Co and Cu, were added to the host network as a doped and not as a substitution. The observed growth in the density and the resulting reduction in molar volume arose from the filling of the interstitial spaces of the glass network by the Co or/and Cu ions, causing shrinking of the interfacial distances and tighter packing. The shrinking of the mean boron-boron separation confirmed the role of the Co or/and Cu ions in filling the interstitial spaces within the studied network, as their penetration into these voids causes them to rival the boron atoms causing their displacement towards each other. As a result of filling the interstitial spaces with Co or/and Cu ions and reducing the mean boron-boron separation, the considered glass network was tightened, which was evident in the increase in OPD and PD as listed in Table 2. On the other hand, the glass containing higher Cu ions concentrations (ErCoCu3 and ErCoCu6) than Co ions (ErCoCu2 and ErCoCu5) showed a higher density due to the higher molecular mass of Cu (63.5 gm/mol) compared to Co (58.933 g/mol). On the other hand, due to the ionic radius of Cu (0.073 nm) is higher than that of Co (0.072 nm), the range of its filling to the network voids had expanded causing a higher reduction in the molar volume for the glass containing higher concentrations of Cu compared to that containing higher concentrations of Co.

The main building block units of the borate network, B–O–B linkage, BO4 units, and BO3 units were observed in the FTIR spectra as shown in Fig. 2a. Some modifications in the intensity and position of the absorption bands with the penetration of Co or/and Cu ions to the host glass network were observed. The Gaussian deconvolution, host glass ErCoCu1 as an example, as shown in Fig. 2b shows the origin of the overlapped bands, which formed the broadbands in the FTIR spectra and examines the occurred structural modifications within the network as a result of Co or/and Cu inclusion.

(a) ATR-FTIR spectra of the considered ErCoCu1-6 glasses and (b) The deconvoluted spectra of ATR-FTIR of ErCoCu1 glass as an example.

In the host glass ErCoCu1, nineteen primary bands have appeared at 643, 684, 733, 839, 919, 984, 1018, 1053, 1091, 1185, 1201, 1243, 1269, 1329, 1357, 1377, 1404, 1419, and 1455 cm−1. The characteristic bands of B–O–B bending vibrations in BO3 triangles, which centered at 690 cm−1 decomposed to 643 cm−1 and 684 & 733 cm−1. The band at 643 cm−1 refers to the asymmetric bond bending vibrations of BO3, while that are 684 and 733 cm−1 refers to symmetric bond bending vibrations 28,29,30,31,32,33. Co ions inclusion (ErCoCu2 glass) increased the intensity and relative area of this band, while an opposite trend was observed with Cu ions inclusion (ErCoCu3). This behavior reflects the network richness of the glass containing 1 mol% of Co ions by B–O–B bending vibration compared to that containing 1 mol% of Cu ions. In the glass containing the mixture of Co and Cu ions (ErCoCu4, ErCoCu5, and ErCoCu6), it was observed that the role of Co ions in enhancing the intensity and relative area of this band is dominant. Finally, a shift towards the higher energy occurred in the glass containing 0.5 mol% of Co and 0.5 mol% of Cu while the relative area increased. The deconvolution of BO4 unit broadband, which appeared here in the spectral region 770–1120 cm−1 emerged six absorption bands at 839, 919, 984, 1018, 1053, and 1091 cm−1. The located band at 839 cm−1 attributed to the B–O stretching vibration of NBOs in BO4 units (\({\mathrm{NBO}}_{{\mathbf{B}\mathbf{O}}_{4}}\))28,29,34,35. This band also may have arisen as a result of the Pb–O bond vibration of PbOn pyramidal units36. The bands at 919, 984, 1018, 1053, and 1091 cm−1 refer to the B–O stretching vibrations units in different structural groups; di, tri, meta, pyro, and ortho borate chains 35,36,37. Finally, ten bands arose as a result of resolving the BO3 broadband in the spectral range of 1125–1500 cm−1. The B–O asymmetric stretching vibrations of NBO of trigonal atoms (\({\mathrm{NBO}}_{{\mathbf{B}\mathbf{O}}_{3}}\)) was observed at 1243 cm−136,37,38,39. The rest of the ten bands, which appeared at 1185, 1201, 1269, 1329, 1357, 1377, 1404, 1419, and 1455 cm−1 arose due to the symmetric and asymmetric of B–O stretching vibrations of trigonal [BO3]3− units in various structural groups; di, tri, meta, pyro, and ortho borate chains28,29,36,37,38,39,40,41. Generally, the inclusion of Co or/and Cu ions to the considered glass network caused a reduction in intensity and relative area of the 839 cm−1 (\({\mathrm{NBO}}_{{\mathbf{B}\mathbf{O}}_{4}}\) band), while an augmentation in both of them was observed for the 1243 cm-1 band (\({\mathrm{NBO}}_{{\mathbf{B}\mathbf{O}}_{3}}\) band) refereeing to the conversion of BO4 units to BO3 ones. The penetration of Co or/and Cu ions led to the enrichment of the glass network with non-bridging oxygens (NBOs) units compared to the bridging (BOs) ones, which is evident from the behavior of N3 and N4 listed in Table 2.

Figure 3 shows the recorded Raman spectra for the considered glasses and their deconvolutions (host glass ErCoCu1 as an example). In Fig. 3a, the observed band in the low energy region 50–125 cm−1 arose due to the vibrational modes of BO3 and BO4 units41. In the deconvolution of host glass ErCoCu1 (in the spectra range 200–1000 cm−1), twelve bands are appeared at 320, 345, 391, 473, 534, 563, 623, 686, 749, 803, 842, and 882 cm−1 as shown in Fig. 3b. The lower frequency bands 320, 345, and 391 cm−1 usually refers to the rotational and vibrational modes of metal–oxygen, here 320 and 345 cm−1 arose as a result of the stretching vibrations and bending mode of Zn–O in ZnO4 structural units42,43, while that at 391 cm−1 due to Pb–O bonds in PbO3 structural units44. The isolated diborate groups of the considered borate network appeared at 473 cm−145. The centered band at 534 cm−1 arose as a result of the deformation mode of B–O–B linkage41, while that appeared at 563 cm−1 arose due to the destruction of diborate groups and the formation of “'loose” BO4ˉ units46. The band at 623 cm−1 arose due to the symmetric stretching of metaborate rings, while that at 686 cm−1 assigned to pentaborate groups45,46,47,48,49,50. The centered band at 623 cm−1 also signifies the formation of a bending mode of the Pb–O–B links45. The appeared band at 749 cm−1 arose as a result of the symmetric breathing vibrations of six-member rings with one or two BO4 tetrahedra48,49. The boroxol ring breathing of the considered borate network appeared at 803 cm−147,51,52. The pyroborate vibrations and ortho-borate groups arose at 842 and 882 cm−1 respectively50,53.

(a) Raman spectra of the considered ErCoCu1-6 glasses and (b) The deconvoluted spectra (host glass ErCoCu1 as an example).

The thermal profile of the considered glasses and the estimated glass transition temperatures \({T}_{g}\) are shown in Fig. 4a,b. As shown in Fig. 4b, the glass transition temperature of the host glass ErCoCu1 appeared at 465 C. With the penetration of Co or/and Cu ions into the considered host glass network, the glass transition temperatures shrunk as shown in Fig. 4b. The observed reduction in the \({T}_{g}\) arose due to the conversion of the higher bond dissociation energy BO4 (62.8–82.2 kJ/cm3) to the lower one BO3 (15.6–16.4 kJ/cm3)54,55, which is clearly shown in Table 2 in the behavior of N3 and N4. The occurred contraction in the \({T}_{g}\) was entirely in tune with the concentration of BO3 within the glass network, where the glasses containing higher concentrations of BO3 showed a lower glass transition temperature than those containing lower concentrations.

(a) DSC profile of the considered glasses and (b) Variation of the glass transition temperature with Co or/and Cu ions.

In the host glass ErCoCu1, a band at 308 nm and ten of the characteristic absorption bands of Er3+ ion at 346, 384, 426, 522, 546, 650, 800, 980, 1512, and 1554 nm have appeared as displayed in Fig. 5a. The absorption band located at 308 nm arose due to of the electron transition in the non-bridging oxygen and/or the electron transition in the divalent Pb2+ ions56,57. The centered bands at 346, 384, 426, 522, 546, 650, 800, 980, and 1554 nm are attributed to the occurred transitions in Er3+ ion between the ground state 4I15/2 and the excited states 2K15/2, 4G11/2, 4F3/2, 2H11/2, 4S3/2,4F9/2, 4I9/2, 4I11/2, and 4I13/2 respectively58,59,60,61. The observed band at 1512 nm arose as a result of the split 4I13/2 level59,60. In Co doped glass ErCoCu2 as shown in Fig. 5a, two broadbands appeared in the spectral region of 400–650 nm and 1250–1500 nm in addition to the presence of the bands at 1512 and 1554 nm, which results from 4I15/2 \(\to \) 4I13/2 transition as mentioned previously59,61. The deconvolution of the appeared two broadbands generated ten bands at 452, 472, 522, 566, 610 1272, 1310, 1346, 1432, and 1448 nm as displayed in Fig. 5b. The two bands at 452 and 522 nm arose due to the transition 4I11/2 \(\to \) 4F5/2 and 4I15/2 \(\to \) 2H11/2 in Er3+ ions59,60. The located bands at 472 and 566 nm arose due to the transitions 4T1g(F)\(\to \) 2T2g(F) in the octahedral Co2+ and spin-forbidden transitions 4A2g(4F)\(\to \) 4T1g(4P) in the tetrahedral Co2+, while that at 610 nm arose due to 5T2g \(\to \) 5Eg transition in the octahedral Co3+32,62,63,64,65. The ground state 4F of tetrahedral field of Co2+ splits to 4A2, 4T2, and 4T1, while 2G splits to 2A1g (G), 2T1g(G), 2T2g(G), and 2Eg(G) levels66,67. Moreover, 4P only transforms to 4T1 (4P) level.

(a) The obtained optical absorption spectra of the considered glasses and the deconclusion of (b) ErCoCu2 and (c) ErCoCu3 glasses.

So, the bands centered at 1272, 1310, 1432, and 1448 nm arose as a result to the transition between the ground state \({\Gamma }_{8}\)(4A2, 4F) and the excited states \({\Gamma }_{6}, {{\Gamma }_{7+8},\Gamma }_{7} \mathrm{and }{\Gamma }_{8}\) of 4T1(4F)66,67,68,69,70 due to the first and second-order spin–orbit coupling effects. The absence of the three bands, which appeared at 346, 384, and 426 nm in ErCoCu1 in this sample, maybe due to their overlap with the two bands appearing at 452 and 472 nm. In Cu doped glass ErCuCo3, in addition to the bands located at 288, 314, 354, 384, 414, 492, 522, 548, 984, 1540, and 1584; a broadband appeared in the region of 740–1140 nm and deconvoluted to 838, 908, 984, and 1058 nm as shown in Fig. 5c. The copper ion usually exists in the two most stable valence states, Cu+ and Cu2+. The fulfilled 3d10 configuration cuprous ion Cu+ shows an absorption band in the UV-blue region due to the 3d10 → 3d9 4s1 transition, therefore the centered band at 288 nm is refers to the existence of Cu+ ion in the ErCoCu3 glass71,72. For copper Cu2+, which is usually present in octahedral coordination, during the melting process; a splitting in the d-orbitals into the doubly degenerate 2 \({E}_{g}\) (higher energy) and the triply degenerate 2 \({T}_{2g}\) (lower energy) occurs. Moreover and due to the tetrahedral distortion, 2Eg splits to 2 \({B}_{2g}\)(\({dx}^{2}-{y}^{2}\)) and 2 \({A}_{2g}\)(\({dz}^{2}\)), while 2T2g splits to 2 \({B}_{2g}\)(\({d}_{xy})\) and 2 \({E}_{g}\)(\({d}_{xz},{d}_{yz})\) through the Jahn–teller effect, which causes a breadth in the shape of the formed peak. Hence, the located bands at 838 (11,933 cm−1), 908 (11,013 cm−1), and 1058 nm (9452 cm−1) are assigned to 2 \({E}_{g}\to \) 2 \({B}_{1g}\), 2 \({B}_{2g}\to \) 2 \({B}_{1g}\), and 2 \({A}_{1g}\to \) 2 \({B}_{1g}\) transitions respectively73,74,75. The others appeared bands in the ErCoCu3 glass at 314, 354, 384, 414, 492, 522, 548, 984, and 1540 & 1584 nm are assigned to the transition in Er3+ ion from the ground state 4I15/2 to the excited states 2D3/2, 2K15/2, 4G11/2, 4F3/2, 4F7/2, 2H11/2, 4S3/2,4I11/2, and 4I13/2 respectively58,59,76,77. In the ErCoCu4, ErCoCu5, and ErCoCu6 glasses, which contain a mixture of Co and Cu ions, the same broadbands are formed as shown in Fig. 5a in the spectral ranges of 400–650, 740–1140, and 1250–1500 nm signifying the presence of octahedral (Oh) and tetrahedral (Td) of Co2+, tetrahedral of Cu2+, and tetrahedral Co3+ respectively. It is also worth mentioning that, the characteristic band of Cu+ ions is continued to exist in these glasses.

The deduced values of the crystal field splitting coefficient 10Dq, Racah parameters B&C, and nephelauxetic ratio β are listed in Table 3. It was found that the Racah parameters, which generally use to measure the Coulomb repulsion within the d-shell decrease with the increase of Cu ions and a decrease of Co ions concentrations. The observed reduction in Rach parameters refers to the covalency nature of the bonds between Co ions and ligands. On the other hand, the observed reduction in the 10Dq signifies that the Co2+ ions have a strong localization in the considered glass network. Nephelauxetic ratio \(\beta \), which measures the stability of ions (Co2+ ions here) complexes and their interaction mechanisms, was found to be increased with Co ions augmentation and Cu ions reduction. The reported growth in Nephelauxetic ratio values indicated the augmentation in the stability of Co2+ ions in the considered glasses. The 10Dq/B ratio, which measures the interaction strength, showed that the crystal field sites of the considered glasses are within the strong interaction regime and tend toward a strong crystal field.

Tauc relationship between \(h\nu \) and \({(\alpha h\nu )}^{0.5}\) was plotted as shown in Fig. 6a (glass ErCoCu1 as an example) to deduce the values of optical band gap for the considered glass. On the other hand, to estimate the Urbach energy values, a relationship between \(h\nu \) and \(\mathrm{ln}\alpha \) was plotted as shown in Fig. 6b (glass ErCoCu1 as an example). Generally, a reduction in optical band gap and the augmentation in Urbach energy with the addition of Co or/and Cu ions compared to the host glass was observed as listed in Table 3.

(a) Tauc plot and (b) \(h\nu \) vs. \({ln}\alpha \) relation.

There are two main reasons for the occurred reduction in the optical band gap and augmentation in Urbach energy. The general one is the formed non-bridged oxygen NBOs in the energy gap near valence and conduction edges. The NBOs behave like donor centers inside the band gap, which cause its shrinking. Also, the linked excited electrons by the non-bridging oxygen are less tight than those linked by the bridging oxygen, which in turn decreases the optical band gap. The specific one is that (i) the gradual augmentation of Co ions in the octahedral position formed a large number of donor centers leading to overlapping between the trapped excited states of localized electrons on Co2+ sites and the unfilled 3d states on the neighboring Co3+ sites. Hence, a wide extension of the impurity or polaron band in the band gap takes place leading to a reduction in the optical band gap16. (ii) Cu ions like Co create a large number of donor centers. In Cu ions, the trapped excited states of localized electrons are on Cu+ sites and overlap with the unfilled 3d states on the neighboring Cu2+ sites78,79. The width of the formed tails due to the agglomerations of NBO, Co, and Cu in the main band gap and the augmentation of the disorder were clearly confirmed by the obtained values of steepness coefficient S. Inclusion of Co or/and Cu reduce the value of steepness coefficient reflecting the shrinking of the edge broadening confirming the disorder augmentation and band gap reduction. The optical band gap values of the glasses containing Co or/and Cu ranged between 1.62 and 2.23 eV, which means that they have a semiconducting nature. The obtained values of the metallization criterion as listed in Table 3 confirmed the semiconducting nature of the considered glasses. The small values of the metalization criterion of the considered glasses refer that the width of both valence and conduction bands becomes large, generating a narrow band gap and enhancing the tendency of the glass for the semiconducting nature. Moreover, the values of the metallization criterion, which ranged from 0.285 to 0.348 indicated that the considered glasses have non-linear refractive indices, which means those glasses have non-linear optical properties80. The non-linear refractive index of the considered glasses was computed using the equation 81,82.

where \(B=1.26\times {10}^{-9} e{V}^{4}\).

Generally, compared to the host glass ErCoCu1, the glasses containing Co or/and Cu possessed high non-linear refractive indices as listed in Table 3, which arose as a result of the increased disorder within the glass network with the penetration of Co or/and Cu ions as confirmed by Urbach energy. The growth of the non-linear refractive index of the ErCoCu1 with the introduction of Co or/and Cu confirmed the enhancement of the non-linear optical properties of the produced glasses.

Through excitation of ErCoCu1 glass using the 380 nm, three emission bands; one in the blue light region at 488 nm and two in the green region at 520 and 533 nm are generated as shown in Fig. 7a.

(a) Emission spectra of ErCoCu glass series, (b) The corresponding Er-electronic transition, and (c) The CIE1931 chromaticity diagram.

Under 380 nm excitations wavelength, a quite well population of 4G11/2 occurred from the ground state absorption (GSA) 4I15/2 as shown in Fig. 7b. Non-radioactive decay via transition to the 4F7/2 excited state occurred, followed by radiative decay generating three lines of blue-green emission at 488, 520, and 533 nm. Sometimes, multi-photon electron relaxation from the excited state 4S3/2 to 4F9/2 takes place followed by the 4F9/2 \(\to \) 4I15/2 transition, leading to the emission of a red wavelength line, which is not observed here. Not noticing a red emission here means that the 4S3/2 \(\to \) 4F9/2 relaxation is not occurring. No variation in the observed emission bands, in position or intensity, was observed with the inclusion of Co or/and Cu. The absence of any change in the emission spectra means that the used wavelength cannot cause any excitation in the Co or Cu ions. Moreover, no energy transfer occurred between Co and Er3+ or Cu and Er3+.

The appropriate combination of the emitted blue and green emissions generates a green light as shown in the CIE 1931 chromaticity diagram in Fig. 7c. The CIE coordinates of the considered glasses were located at \({x}_{s}=0.192\) and \({y}_{s}=0.517\), which is close to the green light of the National Television System Committee (NTSC). The absence of the effect of Co or Cu ions on the intensity and position of the emission bands was clearly reflected on the coordinates of the generated green color, as they all appeared in the same position without any significant change. Xiaojian Pan et al. obtained almost the same coordinates for the emitted green light from CaNb2O6:Tb3+ phosphor under 260 nm excitation83. The color purity of the emitted green light was calculated by the following relation17

where \(\left({x}_{d}, {y}_{d}\right)\), \(\left({x}_{s}, {y}_{s}\right)\), and \(\left({x}_{i}, {y}_{i}\right)\) are the dominant wavelength’s color coordinates, studied samples color coordinate, and ideal white color coordinates respectively.

The dominant wavelength of the considered glasses is \(\sim \) 516 nm and has coordinates (0.022, 0.780). Here, the color purity of the considered glasses is 42.579%.

Impact of 1 mol% of Co or/and Cu ions on the structural, thermal, optical, and green emission of a host glass of 70B2O3–10Pb3O4–18ZnO–2Er2O3 was explored extensively. Both Co or/and Cu have an effective role in modifying the structural properties of the considered glass network by enriching it with non-bridging oxygen, and the formation of different oxidation states for Co and Cu; Co2+/Co3+ and Cu+/Cu2+. The penetration of Co and Cu ions into the studied glass network resulted in a decrease in the glass transition temperature. The optical absorption spectra indicated to the formation of tetrahedral/octahedral coordination of Co2+, octahedral of Co3+, cuprous Cu+, and octahedral coordination of Cu2+ within the considered glass network. The formed band-tail of Co and Cu ions near valence and conduction band edges reduced the optical band gap of the host glass ErCoCu1 from 2.425 to 2.211 eV, 1.624, 2.189, 2.210, and 2.233 eV for ErCoCu2, ErCoCu3, ErCoCu4, ErCoCu5, and ErCoCu6 respectively, which enhanced their semiconducting nature. Morever, the penetration of Co or/and Cu reduced the metalization criterion by 4.023–18.103%, whlie the non-liner refractive index augmentaed from \(3.644\times {10}^{-11}\) for the host glass ErCoCu1 to \(3.644\times {10}^{-11}\), \(5.272\times {10}^{-11}\), \(18.115\times {10}^{-11}\), \(5.282\times {10}^{-11}\), and \(5.068\times {10}^{-11}\) for ErCoCu2, ErCoCu3, ErCoCu4, ErCoCu5, and ErCoCu6 respectively referring to their sutability for non-linear optical devices. The estimated ligand field parameters referred to the strong localization of Co2+ ions and more covalency and stability within the glass network. A green emission with a color purity 42.579% was produced through pump the host glass by 380 nm. In contrast to the structural, thermal, and optical properties, no effect of Co and Cu ions has appeared on the generated green light. Hence, the studied glasses possessed many properties qualifies them for optoelectronics and nonlinear optics applications.

Data will be made available on request. The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.

Sallam, O. I. et al. Synthesis and modification of photoluminescence and dielectric properties of novel fluorophosphate glass by incorporating different transition metal oxides for optoelectronic applications. Opt. Mater. 136, 113413 (2023).

Article CAS Google Scholar

Zandona, A. et al. Oxidation and coordination states assumed by transition metal dopants in an invert ultrabasic silicate glass. J. Non-Crystall. Solids 603, 122094 (2023).

Article CAS Google Scholar

Abou Hussein, E. M. & Abdel-Galil, A. Synthesis, optical, chemical and electrical characterizations of γ-irradiated transition metal ions reinforced borate glasses. J. Non-Crystall. Solids 610, 122302 (2023).

Article Google Scholar

Kalaia, C. et al. Effect of Transition-metal ions (Ni2+, Cu2+ and Co2+) on the electric and dielectric properties of zinc sodium phosphate. Glass Phys. Chem. 45(6), 503–512 (2019).

Article Google Scholar

Mercier, C., Palavitb, G., Montagne, L. & Follet-Houttemane, C. A survey of transition-metal-containing phosphate glasses. C. R. Chim. 5, 693–703 (2002).

Article CAS Google Scholar

Elbashar, Y. H., Saeed, A. & Moslem, S. S. Spectroscopic analysis of copper calcium phosphate glasses matrix. Nonlinear Opt. Quantum Opt. 0, 1–8 (2016).

Google Scholar

Lei, K. et al. Structure and luminescence properties of Cu+ doped glasses prepared by ion exchange. J. Non-Cryst. Solids 605, 122158 (2023).

Article CAS Google Scholar

Abu-raia, W. A., Aloraini, D. A., El-Khateeb, S. A. & Saeed, A. Ni ions doped oxyflourophosphate glass as a triple ultraviolet-visible-near infrared broad bandpass optical filter. Sci. Rep. 12, 16024 (2022).

Article CAS PubMed PubMed Central Google Scholar

Nanao Ningthemcha, R. K. et al. The effect of transition metal and heavy metal incorporation on the structural, optical and electrical properties of zinc-phosphate ternary glassy system: A comparative study. Mater. Chem. Phys. 278, 125672 (2022).

Article Google Scholar

Bhardwaj, P., Kumar, R., Singh, J., Verma, V. & Kumar, R. A comparative study on the structural, optical, and magnetic behavior of transition metal (Co and Mn) ions substituted Cr2O3 nanoparticles. J. Magn. Magn. Mater. 565, 170247 (2023).

Article CAS Google Scholar

Hota, S. B. et al. Effect of transition metal and alkali oxides on structural, optical and dielectric properties in Zinc-Phosphate amorphous glassy systems. J. Non-Crystall. Solids 609, 122235 (2023).

Article CAS Google Scholar

Negm, H. H., Abdo, M. A. & Sadeq, M. S. Impact of Y2O3 on structural, mechanical and nonlinear optical properties of CrO3–Na2O–B2O3 glasses. Optik 274, 170546 (2023).

Article ADS CAS Google Scholar

Saeed, A. et al. Glass materials in nuclear technology for gamma ray and neutron radiation shielding: A review. Nonlinear Opt. Quantum Opt. 53, 107–159 (2020).

Google Scholar

Sallam, O. I., Abdel-Galil, A. & Moussa, N. L. Tuning of smart cobalt doped borate glasses by electron beam as band-pass filters. Opt. Laser Technol. 162, 109262 (2023).

Article CAS Google Scholar

Sallam, O. I., Madbouly, A. M., Elalaily, N. A. & Ezz-Eldin, F. M. Physical properties and radiation shielding parameters of bismuth borate glasses doped transition metals. J. Alloy. Compd. 843, 156056 (2020).

Article CAS Google Scholar

Saeed, A., Elbashar, Y. H. & El Kameesy, S. U. Towards modeling of copper-phosphate glass for optical bandpass absorption filter. Res. J. Pharma. Biol. Chem. Sci. 6(4), 1390–1397 (2015).

CAS Google Scholar

Singh, V., Devi, C. B. A., Kaur, S., Rao, A. S. & Singh, N. Green emission of Er3+-doped Sr2La8(SiO4)6O2 obtained by a sol-gel method. Optik 243, 167322 (2021).

Article ADS CAS Google Scholar

Ran, W. et al. Application of thermally coupled energy levels in Er3+ doped CdMoO4 phosphors: enhanced solid-state lighting and non-contact thermometry. Mater. Res. Bull. 117, 63–71 (2019).

Article CAS Google Scholar

Divina, R., Evangelin Teresa, P. & Marimuthu, K. Dy3+ ion as optical probe to study the luminescence behavior of Alkali lead bismuth borate glasses for w-LED application. J. Alloys Compd. 883, 160845 (2021).

Article CAS Google Scholar

Bassam, S. A. et al. Physical, structural, elastic and optical investigations on Dy3+ ions doped boro-tellurite glasses for radiation attenuation application. Radiat. Phys. Chem. 206, 110798 (2023).

Article CAS Google Scholar

Saeed, A., Elbashar, Y. H. & El Kameesy, S. U. Study of gamma ray attenuation of high-density bismuth silicate glass for shielding applications. Res. J. Pharm. Biol. Chem. Sci. 6(4), 1830–1837 (2015).

CAS Google Scholar

Ouis, M. A. & Marzouk, M. A. Comparative optical, FTIR and photoluminescence spectral analysis of copper ions in BaO–B2O3, SrO–B2O3 or Bi2O3–B2O3 glasses and impact of gamma irradiation. J. Lumin. 223, 117242 (2020).

Article CAS Google Scholar

Saeed, A., Sobaih, S., Abu-raia, W. A., Abdelghany, A. & Heikal, S. Novel Er3+ doped heavy metals-oxyfluorophosphate glass as a blue emitter. Opt. Quantum Electron. 53, 482 (2021).

Article CAS Google Scholar

El-Batal, A. M., Saeed, A., Hendawy, N., El-Okr, M. M. & El-Mansy, M. K. Influence of Mo or/and Co ions on the structural and optical properties of phosphate zinc lithium glasses. J. Non-Crystall. Solids 559, 120678 (2021).

Article CAS Google Scholar

El-Batal, A. M., Farag, M. A., El-Okr, M. M. & Saeed, A. Influence of the addition of two transition metal ions to sodium zinc borophosphate glasses for optical applications. Egypt. J. Chem. 64(12), 6953–6958 (2021).

Google Scholar

Zeed, M. A., El Aly Saeed, R. M., Shazly, H. M., Mallah, E. & Elesh, E. Double effect of glass former B2O3 and intermediate Pb3O4 augmentation on the structural, thermal, and optical properties of borate network. Optik 272, 170368 (2023).

Article ADS CAS Google Scholar

Elbashar, Y. H., Saeed, A. & Rayan, D. A. Prism method of studying the refractive index for zinc borate sodium glass doped neodymium oxide. J. Ceram. Process. Res. 17(6), 532–536 (2016).

Google Scholar

Abul-Magd, A. A., Abu-Khadra, A. S., Taha, A. M. & Basry, A. A. H. Influence of La3+ ions on the structural, optical and dielectric properties and ligand field parameters of Fe3+ hybrid borate glasses. J. Non-Crystall. Solids 599, 121981 (2023).

Article CAS Google Scholar

Babeer, A. M., El-razek Mahmoud, A. & Morshidy, H. Y. Ligand field parameters, optical, thermal, magnetic, and structural features of ZnO containing cobalt-borate glasses. Mater. Chem. Phys. 302, 127681 (2023).

Article CAS Google Scholar

Kim, B.-S., Lim, E.-S., Lee, J.-H. & Kim, J.-J. Effect of Bi2O3 content on sintering and crystallization behavior of low-temperature firing Bi2O3–B2O3–SiO2 glasses. J. Eur. Ceram. Soc. 27, 819–824 (2007).

Article CAS Google Scholar

Gao, G. et al. Effect of Bi2O3 on physical, optical and structural properties of boron silicon bismuthate glasses. Opt. Mater. 32, 159–163 (2009).

Article ADS CAS Google Scholar

Abul-Magd, A. A., Abu-Khadra, A. S. & Abdel-Ghany, A. M. Influence of La2O3 on the structural, mechanical and optical features of cobalt doped heavy metal borate glasses. Ceram. Int. 47, 19886–19894 (2021).

Article CAS Google Scholar

El-Daly, A. A., Abdo, M. A., Bakr, H. A. & Sadeq, M. S. Structure, stability and optical parameters of cobalt zinc borate glasses. Ceram. Int. 47, 31470–31475 (2021).

Article CAS Google Scholar

Gautam, C., Yadav, A. K. & Singh, A. K. A review on infrared spectroscopy of borate glasses with effects of different additives. ISRN Ceram. 2012, 2356–7872 (2012).

Google Scholar

Othman, H. A., Elkholy, H. S. & Hager, I. Z. FTIR of binary lead borate glass: Structural investigation. J. Mol. Struct. 1106, 286–290 (2016).

Article ADS CAS Google Scholar

Rada, S. et al. Towards modeling gadolinium–lead–borate glasses. Mater. Res. Bull. 45, 69–73 (2010).

Article CAS Google Scholar

Farouk, M., Samir, A., Ibrahim, A., Farag, M. A. & Solieman, A. Raman, FTIR studies and optical absorption of zinc borate glasses containing WO3. Appl. Phys. A 126, 696 (2020).

Article ADS CAS Google Scholar

Rada, S., Culea, M. & Culea, E. Structure of TeO2.B2O3 glasses inferred from infrared spectroscopy and DFT calculations. J. Non-Cryst. Solids 354, 5491–5495 (2008).

Article ADS CAS Google Scholar

Rada, S., Culea, M., Neumann, M. & Culea, E. Structural role of europium ions in lead–borate glasses inferred from spectroscopic and DFT studies. Chem. Phys. Lett. 460, 196–199 (2008).

Article ADS CAS Google Scholar

Balakrishna, A., Rajesh, D. & Ratnakaram, Y. C. Structural and photoluminescence properties of Dy3+ doped different modifier oxide-based lithium borate glasses. J. Lumin. 132, 2984–2991 (2012).

Article CAS Google Scholar

Hivrekara, M. M., Sablea, D. B., Solunkeb, M. B. & Jadhav, K. M. Network structure analysis of modifier CdO doped sodium borate glass using FTIR and Raman spectroscopy. J. Non-Crystall. Solids 474, 58–65 (2017).

Article ADS Google Scholar

Lakshminarayana, G. et al. Structural, thermal and optical investigations of Dy3+-doped B2O3–WO3–ZnO–Li2O–Na2O glasses for warm white light emitting applications. J. Luminescence 186, 283–300 (2017).

Article ADS CAS Google Scholar

Lakshminarayana, G. et al. Physical, structural, thermal, and optical spectroscopy studies of TeO2–B2O3–MoO3–ZnO–R2O (R = Li, Na, and K)/MO (M = Mg, Ca, and Pb) glasses. J. Alloys Compd. 690, 799–816 (2017).

Article CAS Google Scholar

Tirupataiah, C. et al. Characterization, optical and luminescence features of cobalt ions in multicomponent PbO–Al2O3–TeO2–GeO2–SiO2 glass ceramics. Opt. Mater. 88, 289–298 (2019).

Article ADS CAS Google Scholar

Padmaja, G. & Kistaiah, P. Infrared and Raman spectroscopic studies on alkali borate glasses: Evidence of mixed alkali effect. J. Phys. Chem. A 113, 2397–2404 (2009).

Article CAS PubMed Google Scholar

Chatzipanagis, K. I. et al. Structure of lead borate glasses by Raman, 11B MAS, and 207Pb NMR spectroscopies. J. Non-Cryst. Solids 589, 121660 (2022).

Article CAS Google Scholar

Narsimha, B., Chandrasekhar, K., Shareefuddin, M. & Ramadevudu, G. EPR, FTIR and Raman spectroscopic characterization of indium barium borate glasses containing manganese ions. J. Appl. Phys. 15(1), 56–68 (2023).

Google Scholar

Kumar Yadav, A. & Singh, P. A review of the structures of oxide glasses by Raman spectroscopy. RSC Adv. 5, 67583–67609 (2015).

Article ADS Google Scholar

Pascuta, P., Lungu, R. & Ardelean, I. FTIR and Raman spectroscopic investigation of some strontium–borate glasses doped with iron ions. J. Mater. Sci. Mater Electron. 21, 548–553 (2010).

Article CAS Google Scholar

Saeed, A., Elbashar, Y. H. & El Khameesy, S. U. A novel barium borate glasses for optical applications. SILICON 10, 569–574 (2018).

Article CAS Google Scholar

Ahmed, M. R. et al. Infrared and Raman spectroscopic studies of Mn2+ ions doped in strontium alumino borate glasses: Describes the role of Al2O3. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 210, 308–314 (2019).

Article ADS CAS Google Scholar

Gautam, C. R. & Yadav, A. K. Synthesis and optical investigations on (Ba, Sr)TiO3 borosilicate glasses doped with La2O3. Opt. Photon. J. 3, 1–7 (2013).

Article ADS Google Scholar

Ahmed, M. R. & Shareefuddin, M. EPR, optical, physical and structural studies of strontium alumino-borate glasses containing Cu2+ ions. SN Appl. Sci. 1, 209 (2019).

Article Google Scholar

Inaba, S., Fujino, S. & Morinaga, K. Young’s Modulus and compositional parameters of oxide glasses. J. Am. Ceram. Soc. 82(12), 3501–3507 (1999).

Article CAS Google Scholar

Saddeek, Y. B. Effect of B2O3 on the structure and properties of tungsten–tellurite glasses. Philos. Mag. 89(1), 41–54 (2007).

Article ADS Google Scholar

Gomaa, H. M., Moneep, A. M., Bendary, A. A., Yahia, I. S. & Zahran, H. Y. Structural and optical absorption coefficient analysis of barium lead sodium-borate glass doped with graphene nanopowder. Optik 271, 170090 (2022).

Article ADS CAS Google Scholar

Ghoneim, N. A., Abdelghany, A. M., Abo-Naf, S. M., Moustafa, F. A. & ElBadry, Kh. M. Spectroscopic studies of lithium phosphate, lead phosphate and zinc phosphate glasses containing TiO2: Effect of gamma irradiation. J. Mol. Struct. 1035, 209–217 (2013).

Article ADS CAS Google Scholar

Chen, F. et al. Investigation of mid-infrared emission characteristics and energy transfer dynamics in Er3+ doped oxyfluoride tellurite glass. Sci. Rep. 5, 10676 (2015).

Article ADS CAS PubMed PubMed Central Google Scholar

Lisiecki, R. Elz_bieta Augustyn, Witold Ryba-Romanowski, and Michał Zelechower, “Er-doped and Er, Yb co-doped oxyfluoride glasses and glass–ceramics, structural and optical properties. Opt. Mater. 33, 1630–1637 (2011).

Article ADS CAS Google Scholar

Çamiçi, H. C. et al. The role of tungsten oxide in Er3+-doped bismuth-germanate glasses for optical amplification in L-band. Sci. Rep. 13, 8835 (2023).

Article ADS PubMed PubMed Central Google Scholar

Kang, S. et al. Spectroscopic properties in Er3+-doped germanotellurite glasses and glass ceramics for mid-infrared laser materials. Sci. Rep. 7, 43186 (2017).

Article ADS PubMed PubMed Central Google Scholar

Ahmed, R. M., Abou-Laila, M. T. & Taha, E. O. Investigating into physical properties of composites of polymer blends and cobalt chloride irradiated by gamma ray for optical devices development. Mater. Today Commun. 35, 105752 (2023).

Article CAS Google Scholar

Ibrahim, A. & Sadeq, M. S. Influence of cobalt oxide on the structure, optical transitions and ligand field parameters of lithium phosphate glasses. Ceram. Int. 47, 28536–28542 (2021).

Article CAS Google Scholar

Aly Okasha, S. Y., Marzouk, A. H., Hammad, A. M. & Abdelghany,. Optical character inquest of cobalt containing fluoroborate glass. Optik 142, 125–133 (2017).

Article ADS Google Scholar

Wahab, S. A. A. et al. Blue emission: Optical properties of Co2+ doping towards Zn2SiO4 glass-ceramics. Optik 274, 170528 (2023).

Article ADS CAS Google Scholar

Suneel Kumar, A. et al. Physical and spectroscopic features of cobalt ions in multi-component CaF2–ZnO–Bi2O3–P2O5 glass ceramics. J. Alloys Compd. 699, 392–400 (2017).

Article CAS Google Scholar

Torres, F. J., Rodrı’guez-Mendoza, U. R., Lavı’n, V., Ruiz de Sola, E. & Alarco’n, J. Evolution of the structural and optical properties from cobalt cordierite glass to glass-ceramic based on spinel crystalline phase materials. J. Non-Crystall. Solids 353, 4093–4101 (2007).

Article ADS CAS Google Scholar

El-Khateeb, S. A. & Saeed, A. Impact of ligands on the performance of band-stop and bandpass optical filter of cobalt sodium zinc borate glass. Opt. Quantum Electron., accepted.

Serment, B. et al. The versatile Co2+/Co3+ oxidation states in cobalt alumina spinel: How to design strong blue nanometric pigments for color electrophoretic display. RSC Adv. 9, 34125–34135 (2019).

Article ADS CAS PubMed PubMed Central Google Scholar

Choe, S.-H. et al. Optical properties of β-In2S3 and β-In2S3:Co2+ single crystals. Semicond. Sci. Technol. 16, 98–102 (2001).

Article ADS CAS Google Scholar

Padlyak, B. V. et al. Spectroscopy and photoluminescence of complex lead-silicate glass doped with copper. Mater. Res. Bull. 158, 112071 (2023).

Article CAS Google Scholar

Das, B. & Mandal, A. K. A comparative study on copper doped sodium alumina-phosphate glass with conventional and microwave heating. Opt. Mater. 134, 113146 (2022).

Article CAS Google Scholar

Sallam, O. I., Alhodaib, A., Abd El Aal, S. & Ezz-Eldin, F. M. Influence of gamma ray on optical and structural properties of commercial glass enriched with copper oxide. Inorg. Chem. Commun. 124, 108388 (2021).

Article CAS Google Scholar

Bäcka, L. G., Alia, S., Karlssonb, S., Wondraczek, L. & Jonson, B. X-ray and UV-Vis-NIR absorption spectroscopy studies of the Cu(I) and Cu (II) coordination environments in mixed alkali-lime-silicate glasses. J. Non-Crystall. Solids X 3, 100029 (2019).

Article Google Scholar

Bae, B.-S. & Weinberg, M. C. Optical absorption of copper phosphate glasses in the visible spectrum. J. Non-Cryst. Solids 168, 223–231 (1994).

Article ADS CAS Google Scholar

Farag, M. A., Abd-Allah, K., Turky, G. M., El-Okr, M. M., Abu-raia, W. A. & Saeed, A. Blue light-emitting diode of Er3+-doped borate glass for optoelectronics devices. Z. für Naturforschung A (2023).

Saeed, A., Farag, M. A. & Abu-raia, W. A. Er3+ ion doped low phonon energy glass as a white light emitter. Egypt. J. Solids 43, 97–110 (2021).

Article Google Scholar

Stefan, R., Culea, E. & Pascuta, P. The effect of copper ions addition on structural and optical properties of zinc borate glasses. J. Non-Cryst. Solids 358, 839–846 (2012).

Article ADS CAS Google Scholar

Srikumar, T. et al. Photostimulated optical effects and some related features of CuO mixed Li2O–Nb2O5–ZrO2–SiO2 glass ceramics. Ceram. Int. 37, 2763–2779 (2011).

Article CAS Google Scholar

Dimitrov, V. & Komatsu, T. Electronic polarizability, optical basicity and non-linear optical properties of oxide glasses. J. Non-Cryst. Solids 249, 160–179 (1999).

Article ADS CAS Google Scholar

Sadeq, M. S. et al. Compositional dependence of transparency, linear and non-linear optical parameters, and radiation shielding properties in lanthanum, iron and calcium borate glasses. Radiat. Phys. Chem. 212, 111027 (2023).

Article CAS Google Scholar

Tichá, H. & Tichýa, L. Semiempirical relation between non-linear susceptibility (refractive index), linear refractive index and optical gap and its application to amorphous chalcogenides. J. Optoelectron. Adv. Mater. 4(2), 381–386 (2002).

Google Scholar

Pan, X., Bao, L., Chao, L., Chao, K. & Liu, Z. Structural and photoluminescence properties of CaNb2O6:Tb3+ green phosphor: Nanocrystalline TbB6 as a new type efficient activator. Phys. B 623, 413352 (2021).

Article CAS Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Department of Petroleum Applications, Egyptian Petroleum Research Institute (EPRI), Cairo, Egypt

Eman O. Taha

Mathematical and Natural Science Department, Faculty of Engineering, Egyptian Russian University, Cairo, Egypt

Aly Saeed

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

A.S. and E.O.T. participated in suggesting the research point, preparing samples, analyzing and discussing the results, and writing and reviewing the manuscript.

Correspondence to Aly Saeed.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Taha, E.O., Saeed, A. The effect of cobalt/copper ions on the structural, thermal, optical, and emission properties of erbium zinc lead borate glasses. Sci Rep 13, 12260 (2023). https://doi.org/10.1038/s41598-023-39256-6

Download citation

Received: 26 June 2023

Accepted: 22 July 2023

Published: 28 July 2023

DOI: https://doi.org/10.1038/s41598-023-39256-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.